The present invention relates to the technical field of glaze, in particular relates to a porcelain bottle lining glaze, made from the following components by weight: 12 sodium stone 18, Qimen 22 kaolin 26 copies, 5 copies, 3 zirconium silicate spodumene 3 5 copies, 1.5 copies of 1 potato starch ether, alkali free glass 2 4 copies, two fiber zirconium diboride 2 4 copies, 4 copies, 2 Zinc Oxide bentonite 3 6 copies, 1.5 copies of 1 strontium carbonate and stabilizing agent 4 8 copies, 8 copies of 4 modified calcite. The glaze of the invention is non-toxic and can be stably adhered on the surface of the porcelain wine bottle, and the glaze can not be dissolved in alcohol for 20 years under the high concentration alcohol.
【技术实现步骤摘要】
本专利技术涉及釉料
,具体涉及一种瓷质酒瓶内衬釉料。
技术介绍
我国的陶瓷工业源远流长,历史悠久。陶、瓷器所用的原料绝大部分是天然的无机非金属矿物,这些原料通过加工精制、配合、成形、高温物理化学反应,才形成一种与原来组成物质截然不同的新的物质,即是陶瓷。我国陶到瓷发展经过了三个阶段:陶器—原始陶器—瓷器。酒的存在已经有几千年历史,喝酒可以放松、愉悦心情,而且陈年老酒越存放越香,现在很多酒厂都会将酒用瓷质酒瓶封存起来,但是现有的瓷质酒瓶长期沾染酒精,酒瓶会受到一定的腐蚀,从而会影响酒的质量。
技术实现思路
本专利技术所要解决的技术问题在于提供一种瓷质酒瓶内衬釉料,釉料无毒,能稳定附着在瓷质酒瓶表面,在高浓度酒精下浸泡20年釉料都不会溶入酒精,釉料烧制后表面形成致密的防渗透层。本专利技术所要解决的技术问题采用以下技术方案来实现:一种瓷质酒瓶内衬釉料,由以下重量份的组分制成:钠石12-18份、祁门高岭土22-26份、硅酸锆3-5份、锂辉石3-5份、马铃薯淀粉醚1-1.5份、无碱玻璃纤维2-4份、二硼化锆2-4份、氧化锌2-4份、膨润土3-6份、碳酸锶1-1.5份、稳定助剂4-8份、改性方解石4-8份。所述稳定助剂由以下重量份的组分构成:纳米氢氧化铝4-6份、月桂基硫酸钠0.5-1.5份、癸酸1-1.5份、儿茶素1-2份、木犀草素0.5-1.5份、聚乙二醇双硬脂酸酯1-2份;其制备方法是,将各原料混合磨碎成细粉,然后将细粉用40-60KHz超声波处理10分钟,再将细粉混入细粉重量份30%-40%的清水搅拌均匀成浆料,然后将浆料送入烘干机内烘干,烘干后继续磨碎成 ...
【技术保护点】
一种瓷质酒瓶内衬釉料,其特征在于,由以下重量份的组分制成:钠石12‑18份、祁门高岭土22‑26份、硅酸锆3‑5份、锂辉石3‑5份、马铃薯淀粉醚1‑1.5份、无碱玻璃纤维2‑4份、二硼化锆2‑4份、氧化锌2‑4份、膨润土3‑6份、碳酸锶1‑1.5份、稳定助剂4‑8份、改性方解石4‑8份。
【技术特征摘要】
1.一种瓷质酒瓶内衬釉料,其特征在于,由以下重量份的组分制成:钠石12-18份、祁门高岭土22-26份、硅酸锆3-5份、锂辉石3-5份、马铃薯淀粉醚1-1.5份、无碱玻璃纤维2-4份、二硼化锆2-4份、氧化锌2-4份、膨润土3-6份、碳酸锶1-1.5份、稳定助剂4-8份、改性方解石4-8份。2.根据权利要求1所述的一种瓷质酒瓶内衬釉料,其特征在于,所述稳定助剂由以下重量份的组分构成:纳米氢氧化铝4-6份、月桂基硫酸钠0.5-1.5份、癸酸1-1.5份、儿茶素1-2份、木犀草素0.5-1.5份、聚乙二醇双硬脂酸酯1-2份;其制备方法是,将各原料混合磨碎成细粉,然后将细粉用40-60KHz超声波处理10...
【专利技术属性】
技术研发人员:许纯荣,
申请(专利权)人:安徽青花坊瓷业股份有限公司,
类型:发明
国别省市:安徽;34