一种回收塑料生产塑料托盘的制造方法，是通过以下步骤实现的：废塑料检测后，依据测得塑料成份含量比例，在废塑料中添加马来酸酐接聚乙；然后再添加聚辛烯/ 乙烯弹性体，添加比例( 重量)：废塑料120G，添加量为6G ～8G 的马来酸酐接聚乙，15G ～ 20G 的聚辛烯/ 乙烯弹性体；高温充分溶合；造粒；注塑产品。本发明专利技术可提高PP 耐冲出强度和耐低温冲击性。

A manufacturing method of plastic tray for recycling plastics

A method for manufacturing recycled plastic production of plastic pallets, is realized by the following steps: detection of waste plastics, on the basis of the measured content of plastic ratio, adding maleic anhydride with polyethylene in the waste plastics; then add polyoctenamer / ethylene elastomer, adding ratio (weight): waste plastics 120G 6G, adding to maleic anhydride 8G with poly, 15G ~ 20G of polyoctenamer / ethylene elastomer; high temperature fully dissolve; granulation; injection molding products. The invention can improve the resistance of out of strength and resistance to low temperature impact resistance of PP.

【技术实现步骤摘要】
一种回收塑料生产塑料托盘的制造方法
本专利技术涉及一种塑料托盘，特别涉及一种回收塑料生产塑料托盘的制造方法。
技术介绍
塑料托盘是一种用在仓储中的垫物装置。废旧塑料制作托盘由于受其使用年限、使用条件(阳光暴晒)以及酸碱腐蚀等原因，造成塑料的耐冲击强度和韧性降低，使废塑料利用价值不高；如何使废旧塑料能成为塑料托盘的材料是技术人员要考虑解决的技术问题。
技术实现思路
本专利技术需要解决的技术问题是提供了一种回收塑料生产塑料托盘的制造方法，旨在解决上述的问题。为了解决上述技术问题，本专利技术是通过以下步骤实现的：废塑料检测后，依据测得塑料成份含量比例，在废塑料中添加马来酸酐接聚乙；然后再添加聚辛烯/乙烯弹性体，添加比例(重量)：废塑料120G，添加量为6G～8G的马来酸酐接聚乙，15G～20G的聚辛烯/乙烯弹性体；高温充分溶合；造粒；注塑产品。与现有技术相比，本专利技术的有益效果是：可提高PP耐冲出强度和耐低温冲击性。具体实施方式下面结合具体实施方式对本专利技术作进一步详细描述：在废旧塑料改性中，更多的是物理改性，通过高聚物与高聚物的共混改性，来改善一些高聚物的固有特点，在PP中添加PE-g-本文档来自技高网...

【技术保护点】
一种回收塑料生产塑料托盘的制造方法，是通过以下步骤实现的：废塑料检测后，依据测得塑料成份含量比例，在废塑料中添加马来酸酐接聚乙；然后再添加聚辛烯/ 乙烯弹性体，添加比例( 重量) ：废塑料120G，添加量为6G ～8G 的马来酸酐接聚乙，15G ～ 20G 的聚辛烯/ 乙烯弹性体；高温充分溶合；造粒；注塑产品。

【技术特征摘要】
1.一种回收塑料生产塑料托盘的制造方法，是通过以下步骤实现的：废塑料检测后，依据测得塑料成份含量比例，在废塑料中添加马来酸酐接聚乙；然后再添加聚辛烯/乙烯弹性体，添加比例(重量)：废塑料120G，添加量为6G～8G的马来酸酐接聚乙，15G～20G的聚辛烯/乙烯弹性体；高温充分溶合；造...

【专利技术属性】
技术研发人员：徐红亚，
申请(专利权)人：徐红亚，
类型：发明
国别省市：浙江,33