一种聚乙烯亚胺改性生物质炭材料、制备方法及在锂硫电池隔膜改性的应用技术

一种聚乙烯亚胺改性生物质炭材料、制备方法及在锂硫电池隔膜改性的应用，属于锂硫电池技术领域。将生物质多炭材料与聚乙烯亚胺以浸渍法在室温下反应，洗涤干燥后即得到聚乙烯亚胺改性的生物质炭材料。聚乙烯亚胺具有丰富的胺基，对于多硫化锂具有较强的捕获能力。生物质炭具有多级孔结构，比表面积高达2000‑3000m

A polyethyleneimine modified biomass carbon material, preparation method and application in the membrane modification of lithium sulfur battery

A polyethylenimide modified biomass carbon material, preparation method and application in the membrane modification of lithium sulfur battery, which belong to the technical field of lithium sulfur battery. Biomass carbon materials and polyethyleneimine were reacted at room temperature by impregnation. After washing and drying, the biomass carbon materials modified by polyethylenimide were obtained. Polyethyleneimine has a rich amino group and has strong capture ability for lithium sulfide. Biomass carbon has a hierarchical pore structure, specific surface area of up to 2000 3000m

【技术实现步骤摘要】
一种聚乙烯亚胺改性生物质炭材料、制备方法及在锂硫电池隔膜改性的应用
本专利技术属于锂硫电池
，具体涉及一种聚乙烯亚胺改性的生物质炭材料的制备方法，尤其在锂硫电池商业隔膜改进中的应用。
技术介绍
能源危机是当今人类社会面临的重大挑战之一。随着新能源和绿色科技的不断发展，人们对动力电池和移动电源设备的要求越来越高。在此背景下，开发一种高比容量、高稳定性、环境友好的电池具有非常重要的意义。锂硫电池由于其高理论比容量(1675mAh/g)及能量密度(2600Wh/kg),活性物质硫储量丰富、环境友好等特点，成为一种非常具有应用前景的新型电池体系。但是，锂硫电池的一个固有问题就是充放电过程中的多硫化物易溶于有机电解液，导致库伦效率降低、容量衰减、多硫化物的的穿梭以及自放电现象。这些极大的限制了锂硫电池的商业化应用。为了解决这一问题，现有技术通过采用介孔材料浸渍硫、功能高分子包覆硫、亲水性基团修饰硫等作为电池的正极材料，用于限制硫及多硫化物的溶解。但是，这些合成物通常价格昂贵且合成方法复杂，难以实现商业化应用。2012年，德克萨斯大学的Manthiram课题组首次提出隔膜修饰(隔膜改性)的本文档来自技高网...

【技术保护点】
一种聚乙烯亚胺改性生物质炭材料，其特征在于，采用聚乙烯亚胺溶液浸渍改性多孔生物质炭材料，随后经洗涤、干燥即得。

【技术特征摘要】
1.一种聚乙烯亚胺改性生物质炭材料，其特征在于，采用聚乙烯亚胺溶液浸渍改性多孔生物质炭材料，随后经洗涤、干燥即得。2.按照权利要求1所述的一种聚乙烯亚胺改性生物质炭材料，其特征在于，聚乙烯亚胺负载在生物质多孔炭材料上，聚乙烯亚胺改性生物质炭材料比表面积为1000-2500m2/g。3.制备权利要求1或2所述的聚乙烯亚胺改性生物质炭材料的方法，其特征在于，包括以下步骤：步骤(1)：将生物质多孔炭加入到KOH溶液中，搅拌反应后固液分离，用去离子水洗涤生物质炭至中性，干燥得到预处理后的生物质多孔炭；步骤(2)将步骤(1)得到的预处理后的生物质多孔浸渍于聚乙烯亚胺溶液中，充分搅拌，固液分离；步骤(3)将步骤(2)的反应产物用甲醇洗涤数次，干燥后得到聚乙烯亚胺改性的生物质炭。4.按照权利要求1或2的方法，其特征在于，步骤(1)中的KOH浓度为1-3mol/L；生物质多孔炭采用鱼鳞和KOH为原材料，用热处理的方...

【专利技术属性】
技术研发人员：黄雅钦，于帆，
申请(专利权)人：北京化工大学，
类型：发明
国别省市：北京,11