The invention relates to a preparation method of activated carbon, which comprises the following steps: (1) the carbon precursor polymer and foaming agent, mixed solvent is added after the dissolution of 1 3H in 30 100 DEG C; (2) the activated carbon material and activating agent are mixed evenly, and added to the solution 2 stains 5h, and in a vacuum drying box for drying; (3) the step (2) of the sample after drying at high temperature and high pressure sintering furnace, inert gas under the condition of 800 1500 C 10 carbonization 20h, the activated carbon product; compared with the prior art, the porous activated carbon has been in the invention, large specific surface area and high strength, and has broad market demand.
【技术实现步骤摘要】
一种制备活性炭的方法
本专利技术属于活性炭的制备
，尤其涉及一种制备活性炭的方法。
技术介绍
活性炭是常用的吸附剂之一，已在食品卫生、医疗、催化、空分制氮、焦炉气中氢气的回收等方面得到广泛的应用，其吸附性能在很大程度上决定于其孔结构特征。活性炭的孔隙分布呈三分散型，即大孔、中孔和微孔均占一定比例。然而，活性炭的这种三分散型宽分布孔径结构，却在一定程度上制约了活性炭在某些领域的应用。因此，随着社会对专用吸附剂的需求增加，因此对孔径进行有效的控制就成了炭材料研究者所追求的目标。为了制备出更有针对性的活性炭，可以对其孔结构进行改性。目前研究和使用的孔隙结构调节方法主要是碳沉积技术。碳沉积的原理是将有机高分子化合物、烃类气体分子与活性炭接触，在适当的温度下使其裂解析出游离碳，并在大孔和中孔孔隙的入口处沉积碳，从而使孔径缩小，实现产品孔隙均一化。此外，聚合物共混炭化法有望成为一种能够对活性炭孔径进行精细控制的方法。该方法利用两种热稳定性不同、可形成相分离结构的聚合物共混炭化，热稳定性高的聚合物(称为炭前驱体聚合物)经过高温炭化成为炭基体，热稳定性差的聚合物(称为造孔剂...
【技术保护点】
一种制备活性炭的方法，其特征在于，包括以下步骤：(1)将炭前躯体聚合物和发泡剂，混合，加入溶剂后在30‑100℃下溶解1‑3h；(2)将活性炭原料与活化剂混合均匀，并加入到上述溶液中浸渍2‑5h，并在真空干燥箱中进行干燥；(3)将步骤(2)干燥后的样品在高温高压烧结炉中，惰性气体条件下800‑1500℃炭化10‑20h，最后得到活性炭成品。
【技术特征摘要】
1.一种制备活性炭的方法，其特征在于，包括以下步骤：(1)将炭前躯体聚合物和发泡剂，混合，加入溶剂后在30-100℃下溶解1-3h；(2)将活性炭原料与活化剂混合均匀，并加入到上述溶液中浸渍2-5h，并在真空干燥箱中进行干燥；(3)将步骤(2)干燥后的样品在高温高压烧结炉中，惰性气体条件下800-1500℃炭化10-20h，最后得到活性炭成品。2.根据权利要求1所述的制备活性炭的方法，其特征在于,所述的炭前躯体聚合物包括木质素、酚碳酸甲醛树脂、壳聚糖中的一种或几种。3.根据权利要求1所述的制备活性炭的方法，其特征在于,所述的发泡剂包括偶氮二甲酰胺、4,4′-氧代双苯磺酰肼、对甲苯磺酰肼、4,4′-二磺酰肼、二亚硝基五亚甲基四胺中的一种或几种。4.根据权利要求1所述的制备活性炭的方法，其特征在于,所述的溶剂包括甲醇...
【专利技术属性】
技术研发人员：钟传新，王君，
申请(专利权)人：桂林浩新科技服务有限公司，
类型：发明
国别省市：广西,45
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。