聚乙烯吡络烷酮改性的骨水泥及制备方法技术
Polyvinyloloxone modified bone cement and preparation method
The invention relates to Polyvinylpyrrolidone Modified Bone Cement and its preparation method, including powder and curing solution: powder is hemihydrate calcium sulfate, the curing solution is polyvinylpyrrolidone aqueous solution, the concentration is 0.1% to 5%, and the liquid solid ratio is 0.4 ~ 0.6ml/g. A polyvinylpyrrolidone curing solution with a concentration of 0.1% to 5% was prepared. Then, the mixture of liquid and solid ratio was added to the semi hydrated calcium sulfate powder, and the mixture was evenly stirred and solidified at room temperature to form injectable bone cement. Because polyvinylpyrrolidone is a water-soluble polymer, it is odorless, tasteless, almost non-toxic, and has good biocompatibility and strong combination. The bone cement in the invention also has good biocompatibility and biodegradability, and can be used for filling and repairing various bone defects. It is used in the field of tissue engineering and medicine.
【技术实现步骤摘要】
聚乙烯吡络烷酮改性的骨水泥及制备方法
本专利技术涉及一种用于人体硬组织修复的可注射型骨水泥及制备方法，特别是聚乙烯吡络烷酮改性的骨水泥及制备方法；主要用于生物医用材料等领域。
技术介绍
由于意外事故、创伤或疾病会导致骨损坏或骨缺损，传统的外科手术不仅费用昂贵，而且还会给患者带来痛苦。长期以来，为了寻求理想的骨移植材料，许多科研人员不懈的努力着。目前，骨移植材料主要分为三大类：自体骨骨移植材料、异体骨骨移植材料和人工骨骨移植材料。自体骨虽然无免疫排斥反应，但由于其数量有限且会对自身造成二次伤害等缺点而使其在临床应用中受到限制；异体骨虽然数量较自体骨多，但由于其可能存在免疫排斥、供体可能有病毒及社会道德伦理问题等的限制，所以异体骨也不是骨移植材料的最好选择。为了解决以上两种骨移植材料的问题，为了获得理想的骨移植材料，于是，科研工作者们开始研究人工骨。骨水泥是新一代的骨替代材料，在骨缺损的填充、骨移植和骨移植材料的固定等方面具有广泛的应用。生物活性骨水泥由固相和液相两部分组成，固液相按照一定的比例混合后可形成具有可自固化的浆体，该浆体具有任意塑造性。硫酸钙骨水泥(CSC...
【技术保护点】
一种可注射型骨水泥及制备方法,包括粉剂和固化液：其中粉剂为半水硫酸钙，固化液为聚乙烯吡络烷酮水溶液，浓度为0.1％～5％，液固比为0.4～0.6ml/g。
【技术特征摘要】
1.一种可注射型骨水泥及制备方法,包括粉剂和固化液：其中粉剂为半水硫酸钙，固化液为聚乙烯吡络烷酮水溶液，浓度为0.1％～5％，液固比为0.4～0.6ml/g。2.如权利要求1所述的材料,其特征是所述固化液为浓度为0.1％～5％的聚乙...
【专利技术属性】
技术研发人员：成艳琪，李朝阳，梁砚琴，朱胜利，崔振铎，杨贤金，
申请(专利权)人：天津大学，
类型：发明
国别省市：天津,12