The invention discloses a foamed organosilicon material and a preparation method, which belongs to the field of organosilicon technology. Foamed silicone material of the invention comprises the following according to the weight of raw materials: 50 hydroxy silicone oil 80 copies, 10 copies of 5 vinyl silicone oil, silicone oil containing hydrogen 5 20, two two 1 lauric acid butyl tin 2, Ji An base 2 5 copies, 5 10 nanometer calcium carbonate a. Organosilicon foam is prepared by using hydroxyl silicone oil, vinyl silicone oil, hydrogen containing silicone oil and so on as the main raw materials. The foamed organosilicon material has excellent comprehensive mechanical properties, and the bubble hole is uniform, fine and elastic.
【技术实现步骤摘要】
一种发泡有机硅材料及其制备方法
本专利技术涉及一种有机硅材料及其制备方法,具体涉及一种发泡有机硅材料及其制备方法。
技术介绍
软质泡沫材料是泡沫塑料的一大类品种,因柔软、弹性好,广泛应用于工业、农业、交通运输、军事、建筑及日用品等领域。由于其结构的特殊性,故具有许多其它材料所不能同时具备的优异性能,如卓越的耐高温与耐低温性、优良的电绝缘与化学稳定性,良好的耐老化性、突出的表面活性、憎水防潮和生理惰性等。通常作为阻尼、隔音、减震、电绝缘封装等材料应用于航空航天领域作为航天器、火箭等的轻质、耐高温、抗湿材料等。现有软质泡沫材料机械性能较差,且泡孔不均匀,细密和弹性也较差。
技术实现思路
有鉴于此,本申请提供一种发泡有机硅材料,该发泡有机硅材料具有优异综合机械性能,且泡孔均匀,细密和弹性良好。为解决以上技术问题,本专利技术提供的技术方案是一种一种发泡有机硅材料,其特征在于:包括以下按照重量份数计的原料:羟基硅油50-80份,乙烯基硅油5-10份,含氢硅油5-20份,二月桂酸二丁基锡1-2份,季氨碱2-5份,纳米级碳酸钙5-10份。优选的,所述发泡有机硅材料包括以下按照重量份数计的原料:羟基硅油70份,乙烯基硅油8份,含氢硅油10份,二月桂酸二丁基锡1份,季氨碱4份,纳米级碳酸钙8份。本专利技术还提供一种发泡有机硅材料的制备方法,包括以下工艺步骤:A、在一个三口反应器内加入羟基硅油和二月桂酸二丁基锡;在120-150℃下预聚1-3h,然后在160-180℃下预聚1-3h;B、加入乙烯基硅油、纳米级碳酸钙和季氨碱,搅拌混合;加入含氢硅油,快速搅拌;C、倒入模具,自动发泡 ...
【技术保护点】
一种发泡有机硅材料,其特征在于:包括以下按照重量份数计的原料:羟基硅油50‑80份,乙烯基硅油5‑10份,含氢硅油5‑20份,二月桂酸二丁基锡1‑2份,季氨碱2‑5份,纳米级碳酸钙5‑10份。
【技术特征摘要】
1.一种发泡有机硅材料,其特征在于:包括以下按照重量份数计的原料:羟基硅油50-80份,乙烯基硅油5-10份,含氢硅油5-20份,二月桂酸二丁基锡1-2份,季氨碱2-5份,纳米级碳酸钙5-10份。2.根据权利要求1所述的一种发泡有机硅材料,其特征在于:包括以下按照重量份数计的原料:羟基硅油70份,乙烯基硅油8份,含氢硅油10份,二月桂酸二丁基锡1份,季氨碱4份,纳米级碳酸钙8份。3.根据权利要求1或2所述的一种发泡有机硅材料的制备方法,其特征在于:包括以下工艺步骤:A、在一个三口反应器内加入羟基硅油和二月桂酸二丁基锡;在120...