The invention discloses a high temperature resistant paint and preparation method thereof, prepared from the following raw materials: the weight fraction of silicone resin 100, calcium carbonate 10 20 copies, 10 copies, 5 graphite carbon black 2 5 copies, 20 copies, 10 flame retardant modified hydroxyl acrylic resin 10 20 1, 2 mica powder. The preparation method comprises the following steps: (1) the silicone resin, carbon black, graphite powder, flame retardant, modified mixed hydroxyl acrylic resin and mica powder evenly, heated to 200 250 DEG C, stirring and heat preservation 1H mixed homogeneous melt; (2) the light calcium carbonate into steps (1) melt in the heat and continue to 1H, the melt obtained is high temperature resistant paint. Compared with the prior art, the invention has the beneficial effect of adding alumina powder to make the paint flame retardancy good, and adding light calcium carbonate. When it burns at high temperature, it will harden into ceramic layer and form a flame retardant layer.
【技术实现步骤摘要】
一种耐高温油漆及其制备方法
本专利技术属于涂料领域，尤其涉及一种耐高温油漆及其制备方法。
技术介绍
油漆作为一种日常生活中极为常见的产品，现有的各类油漆普遍存在不耐高温的缺点，对于此类油漆一旦发生火灾，其将成为一种助燃剂，使得火势越烧越旺，从而给人们造成巨大的经济损失。
技术实现思路
为了解决上述技术问题，本专利技术的目的在于提供一种耐高温性能好，且具备一定阻燃性能的油漆。为实现上述目的，本专利技术的技术方案是：一种耐高温油漆，由以下重量分数的原料制成：有机硅树脂100份、轻质碳酸钙10-20份、石墨粉5-10份、炭黑2-5份、阻燃剂10-20份、改性羟基丙烯酸树脂10-20份、云母粉1-2份。上述技术技术方案中，优选的，所述油漆由以下重量分数的原料制成：有机硅树脂100份、轻质碳酸钙12-18份、石墨粉6-9份、炭黑3-4份、阻燃剂12-18份、改性羟基丙烯酸树脂12-18份、云母粉1.3-1.7份。上述技术技术方案中，进一步优选的，所述油漆由以下重量分数的原料制成：有机硅树脂100份、轻质碳酸钙15份、石墨粉8份、炭黑3.5份、阻燃剂15份、改性羟基丙烯酸树脂15...
【技术保护点】
一种耐高温油漆，其特征在于，由以下重量分数的原料制成：有机硅树脂100份、轻质碳酸钙10‑20份、石墨粉5‑10份、炭黑2‑5份、阻燃剂10‑20份、改性羟基丙烯酸树脂10‑20份、云母粉1‑2份。
【技术特征摘要】
1.一种耐高温油漆，其特征在于，由以下重量分数的原料制成：有机硅树脂100份、轻质碳酸钙10-20份、石墨粉5-10份、炭黑2-5份、阻燃剂10-20份、改性羟基丙烯酸树脂10-20份、云母粉1-2份。2.根据权利要求1所述的耐高温油漆，其特征在于，由以下重量分数的原料制成：有机硅树脂100份、轻质碳酸钙12-18份、石墨粉6-9份、炭黑3-4份、阻燃剂12-18份、改性羟基丙烯酸树脂12-18份、云母粉1.3-1.7份。3.根据权利要求2所述的耐高温油漆，其特征在于，包括以下重量分数的原料制成：有机硅树脂100份、轻质碳酸钙15份、石墨粉8份、...