The invention relates to the field of coating technology, discloses a dispersive coating and its application, and discloses a drying room for tobacco leaves and a food storage room coated with dispersed paint on the inner wall. Including the dispersion coating: 8 to 12 parts by weight of aluminum silicate, 2 - 4 weight portions of layered silicate, 10 - 30 by weight of titanium dioxide, 15 - 30 weight portions of silicon resin, 2 - 35 weight portions of calcium carbonate, 0 - 4 by weight of a non crystal vitreous body and ceramic hollow body, 0 - 5 weight additive in 10 - 100, and the weight of water. The dispersing paint provided by the invention can reduce the energy consumption in the tobacco drying process, and ensure that the heat energy distribution in the drying chamber and the storage room is stable and even, and it does not form water vapor concentration in the upper layer of the drying chamber.
【技术实现步骤摘要】
分散性涂料及其应用
本专利技术涉及涂料
，尤其涉及一种分散性涂料及其应用，还涉及内壁涂覆分散性涂料的烟叶烘干室和食品储存室。
技术介绍
烟草加工工艺中一个重要的步骤是烘干环节。烘干消耗能量，不但产生成本，同时也导致二氧化碳排放，对环境产生负面影响。另外，烘干环节也对产品的最终质量起到决定性作用。在烘干过程中，空气湿度管理至关重要。湿气及其在烤烟房内的分布决定了烟叶上是否滋生霉菌。烟叶霉变不但使烟草质量下降，而且对烟民健康造成额外的风险。这两个因素是品质和商业成功的主要组成部分。概括而言，本专利技术的目的是减少烟草烘干过程中的能量消耗，同时保证烘干室和储存室内热能的良好分布。特别是湿气必须得到有效控制，防止烟叶发生霉变。
技术实现思路
本专利技术的目的在于提供一种分散性涂料，通过利用本专利技术的分散性涂料可以减少烟草烘干过程中的能量消耗，同时保证烘干室和储存室内热能的良好分布。在一方面，本专利技术提供一种由以下组分组成的分散性涂料:8–12重量份铝硅酸盐，2–4重量份层状硅酸盐，10–30重量份二氧化钛，15–30重量份硅树脂,2–35重量份碳酸钙，0–4重量份非...
【技术保护点】
一种由以下组分组成的分散性涂料，其特征在于，包括：
【技术特征摘要】
2017.08.25 DE 102017119529.71.一种由以下组分组成的分散性涂料，其特征在于，包括：2.如权利要求1所述的分散性涂料，其特征在于，所述分散性涂料包含9–11重量份铝硅酸盐。3.如权利要求1或2所述的分散性涂料，其特征在于，所述铝硅酸盐至少包括沸石。4.如权利要求1所述的分散性涂料，其特征在于，所述铝硅酸盐以粒子混合物形式存在，所述粒子混合物包括粒径为1～200μm和400～500μm的两种颗粒，所述两种颗粒分别通过第一级和第二级筛分选取。5.如权利要求4所述的分散性涂料，其特征在于，所述第一级筛分与第二级筛分所得的颗粒之间重量比在1:0.5至1:1的范围内。6.如权利要求5所述的分散性涂料，其特征在于，所述第一级筛分与第二级筛分所得...
【专利技术属性】
技术研发人员：布兰德·布尔克哈德，邦德·沃尔夫冈，
申请(专利权)人：米格材料创新有限公司，
类型：发明
国别省市：德国,DE