The invention relates to a special external mold oil for high speed drawing of copper tubes. The raw material components and their weight percentages are: polyisobutene 20 - 35%, polyol ester oil additive 10 - 15%, copper corrosion inhibitor 0.05 - 0.3%, antioxidant 0.05 - 0.5%, and the rest is base oil. The invention provides a high speed drawing special brass outer mold oil with high temperature resistance and high volatile and low smoke properties of base oil, polymer and oily agent, avoid drawing oil smoke in high temperature conditions when drawing, avoiding the preparation process and use of pollution, but also possesses good lubricity.
【技术实现步骤摘要】
一种铜管高速拉拔专用外模油
本专利技术属于化工产品领域,特别涉及一种铜管高速拉拔专用外模油。
技术介绍
制冷工业用的高质量内螺纹铜管的加工分为胚管(光管)加工和胚管内壁内螺纹成型等两部分。内螺纹胚管(铜光管)的拉拔加工大多是在高速圆盘拉伸机上进行的,拉拔速度最高可达1000m/min以上。铜管在如此苛刻的拉拔条件下,很容易造成外表面的擦伤和缺陷。铜管拉拔润滑油作为铜管拉拔加工的专用工艺润滑油,是保证铜管顺利加工和表面质量的关键因素。目前高速的铜管拉拔工艺,不仅要求润滑油有良好的粘附性、润滑性和耐高温挥发性能,而且还要易于被清洗剂清洗。也就是说,在保证铜管外表面不因润滑不良而造成擦伤的前提下,要尽可能地避免油烟对工作环境的污染,尽可能地提高铜管外表面的光洁度。目前国内外普遍采用的铜管外模油,都不能很好地满足铜管高速圆盘拉伸机对外模油的润滑、清洗双重要求,主要存在润滑不足,易造成铜管表面擦伤;产品发烟,污染环境,且难于清洗。随着我国内螺纹铜管生产线的不断引进和国产化,内螺纹铜管拉伸专用润滑剂的国产化已迫在眉睫。我公司开发了铜拉拔专用外模油,并采用了自建的评价方法进行了评价。
技术实现思路
本专利技术的目的在于克服现有技术的不足之处,提供一种润滑性能好、绿色环保的铜管高速拉拔专用外模油。本专利技术解决其技术问题所采用的技术方案是:一种铜管高速拉拔专用外模油,其原料组分及其重量百分比分别为:而且,所述聚异丁烯的相对分子量为1000-3000。而且,所述基础油为150BS基础油。上述铜管高速拉拔专用外模油的制备方法为:向基础油中依次加入聚异丁烯、多元醇酯油性剂、铜腐蚀抑 ...
【技术保护点】
一种铜管高速拉拔专用外模油,其特征在于:其原料组分及其重量百分比分别为:
【技术特征摘要】
1.一种铜管高速拉拔专用外模油,其特征在于:其原料组分及其重量百分比分别为:2.根据权利要求1所述的铜管高速拉拔专用外模油,其特征在于:所述聚异丁烯的相对分子量为1000-3000。3.根据权利要求1所述的铜管高速拉拔专用外模油,其特征在于:所述基础油为150BS基础油。4.根据权利要求...
【专利技术属性】
技术研发人员:孙兰凤,
申请(专利权)人:天津市澳路浦润滑科技股份有限公司,
类型:发明
国别省市:天津,12