The invention relates to a water-soluble Aluminum Alloy sheet stamping oil, components of the raw material and the weight percentage are: pentaerythritol monooleate 3 - 8%; extreme pressure agent 2 - 5%; 5 - 12% sodium petroleum sulfonate emulsifier; 4 - 10%; 0.5 - 4% inhibitor; nonionic surfactant 0.5 2%; fatty alcohol polyoxyethylene ether 1 - 5%; aluminum phosphate amine neutralization corrosion inhibitor 0.2 - 1.5%; defoaming agent 0.03 - 0.1% MBM 0.5 - 1.5%; preservatives; balance base oil. The water-soluble punching oil for aluminum alloy plate is prepared by highly refined paraffin base oil and emulsifier, extreme pressure agent, synthetic ester oil agent, surfactant, defoamer, bactericide and rust inhibitor. Low odor, excellent extreme pressure, corrosion resistance and lubrication, suitable for aluminum alloy sheet metal stamping, stretching, punching and other processing technology.
【技术实现步骤摘要】
一种铝合金板材水溶性冲压油
本专利技术属于化工产品领域,特别涉及一种铝合金板材水溶性冲压油。
技术介绍
随着能源供应与社会需求之间的矛盾日益加剧,全球各大汽车制造厂商加大了对节能、降耗产品研究与开发的力度。铝合金板质量轻、比强度高,日益成为汽车覆盖件青睐的对象,汽车覆盖件的轻型化成为解决这一矛盾最直接的措施之一。但铝合金板塑性差,成形时生成的新金属表面活性强、极易粘着模具,容易被氧化成坚硬、脆性的耐磨层。这与铝合金板料在成形时的摩擦润滑状态有密切关系。因此,要求冲压油应具备优良的抗腐蚀性能、防锈性能、润滑性能、抗硬水能力、清洗性能和冷却性能。目前国内市场上水溶性的铝合金板冲压油很少,且存在冲压完成后工件表面易腐蚀变色,颜色发暗等问题。本专利技术产品具有优良的铝缓蚀性能、优良的润滑性能、抗硬水性能和乳化稳定性。冲压完成的工件表面光亮,在工序间存放一周内无变色和腐蚀。
技术实现思路
本专利技术的目的在于克服现有技术的不足之处,提供一种具有良好缓释功能的环保型铝合金板材水溶性冲压油。本专利技术解决其技术问题所采用的技术方案是:一种铝合金板材水溶性冲压油,其原料组分及其重量百分比分别为:而且,所述基础油为环烷基基础油。而且,所述乳化剂为油酸三乙醇胺。而且,所述铝缓蚀剂为胺中和磷酸酯。而且,所述防锈剂为诺泰公司生产的NEUF486。而且,所述非离表面活性为OP-10。而且,所述极压剂为磷酸酯。上述铝合金板材水溶性冲压油的制备方法为:按配比将所有原料混合,搅拌均匀,静置20分钟,即得成品。本专利技术的优点和积极效果是:本专利技术提供的铝合金板材水溶性冲压油是由高度精制的石 ...
【技术保护点】
一种铝合金板材水溶性冲压油,其特征在于:其原料组分及其重量百分比分别为:
【技术特征摘要】
1.一种铝合金板材水溶性冲压油,其特征在于:其原料组分及其重量百分比分别为:2.根据权利要求1所述的铝合金板材水溶性冲压油,其特征在于:所述基础油为环烷基基础油。3.根据权利要求1所述的铝合金板材水溶性冲压油,其特征在于:所述乳化剂为油酸三乙醇胺皂。4.根据权利要求1所述的铝合金板材水溶性冲压油,其特征在于:所述铝缓蚀剂为胺中和磷酸酯。5.根据权利要求1所述的铝合金板...
【专利技术属性】
技术研发人员:孙兰凤,
申请(专利权)人:天津市澳路浦润滑科技股份有限公司,
类型:发明
国别省市:天津,12