一种木质素基高比表面积碳材料的制备方法技术

本发明专利技术公开了一种木质素基高比表面积碳材料的制备方法，该方法采用木质素作为碳材料前驱体，将木质素配制成水溶液，经冷冻干燥后得到木质素气凝胶，将得到的木质素气凝胶置于管式炉中于氩气气氛中碳化，冷却后即得到所述的高比表面积碳材料。本发明专利技术通过冷冻干燥、高温碳化制备得到高比表面积、低密度的碳气凝胶材料，避免了活化过程，相比现有通过先碳化再活化的制备方法，有效降低了能耗，避免了污染环境。

Preparation of a lignin based high specific surface area carbon material

The invention discloses a preparation method of lignin based high specific surface area of carbon material, the method of using lignin as carbon precursor, lignin preparation of aqueous solution, after freeze-drying by lignin aerogels, will get the lignin aerogel in a tube furnace in argon atmosphere carbide, carbon material with high surface area after cooling to obtain the. The invention can prepare high carbon and aeration material with high specific surface area and low density by freeze-drying and high-temperature carbonization, avoiding the activation process, and effectively reducing energy consumption and avoiding polluting environment compared with the existing preparation method through carbonization and reactivation.

【技术实现步骤摘要】
一种木质素基高比表面积碳材料的制备方法
本专利技术属于碳材料制备领域，具体涉及一种木质素基高比表面积碳材料的制备方法。
技术介绍
多孔碳材料是指具有高孔隙率以及大比表面积的碳基材料，由于其较大的比表面积、独特的孔道结构以及丰富的表面官能团，是最有前景的一类吸附材料，同时在能源、环保、复合材料、催化剂载体等许多关键领域也有着重要用，因此制备高比表面积的碳材料具有重要意义。而目前制备高比表面积碳材料的方法多是根据先进行高温碳化，再通过物理或化学活化的方式制备，而活化过程能耗高或是污染严重。如公开号为CN105271227A的专利技术专利公开了一种高比表面积多孔炭材料的制备方法，该方法将碳前驱体先在氮气保护下进行碳化，再利用氢氧化钾在氮气保护下高温煅烧，最后使用盐酸除去杂物，并洗涤干燥后得到具有高比表面积的多孔炭材料。该方法虽然可以制备表面积较高的多孔炭材料，但是制备过程中需要使用活化剂进行活化，该过程会产生大量废弃的活化剂，如氢氧化钾等，同时还需要使用酸对活化后的碳材料进行清洗，从而使得制备过程不仅能耗高，而且污染环境。
技术实现思路
针对现有技术存在的上述不足，本专利技术的目的是提供一种木本文档来自技高网...

【技术保护点】
一种木质素基高比表面积碳材料的制备方法，其特征在于，将木质素配制成水溶液，经冷冻干燥后得到木质素气凝胶，将得到的木质素气凝胶置于管式炉中于氩气气氛中600~1000℃碳化，冷却后即得到所述的高比表面积碳材料。

【技术特征摘要】
1.一种木质素基高比表面积碳材料的制备方法，其特征在于，将木质素配制成水溶液，经冷冻干燥后得到木质素气凝胶，将得到的木质素气凝胶置于管式炉中于氩气气氛中600~1000℃碳化，冷却后即得到所述的高比表面积碳材料。2.根据权利要求1所述的木质素基高比表面积...

【专利技术属性】
技术研发人员：陈凤贵，
申请(专利权)人：长江师范学院，
类型：发明
国别省市：重庆,50