The invention relates to a forklift accessory, in particular to a high toughness forklift fork, which belongs to the field of mechanical manufacture. The invention of high toughness fork by steel material, the steel material comprises the following components: C:0.30 weight percentage of 0.35%, Si:0.15 0.35%, Mn:1.10 1.40%, Cr:0.02 0.04%, Ti:001 0.03%, B:0.002 0.004%, Ta:0.1 0.2%, N:0.01 0.03%, Al2O3 0.1 whiskers: 0.2%, P: 0.03%, S: 0.03%. After adjusting the composition and weight percentage of the steel, the invention further adjusts the manufacturing method of forklift truck fork which can improve the strength and toughness of the steel, greatly improves the toughness of the steel and so on, and meets the requirements of the fork.
【技术实现步骤摘要】
一种高韧性叉车货叉
本专利技术涉及一种叉车配件，尤其涉及一种高韧性叉车货叉，属于机械制造领域。
技术介绍
货叉是叉车的属具，相当于挂装在叉车上的机械手，使叉车成为一种多用途高效率的物料搬运工具，能对几乎任何可以想象到的搬运对象进行叉、夹、推、拉、侧移和旋转等作业，从而提高物流效率，降低生产成本，避免产品破损，节省仓储空间。叉车货叉广泛应用于仓储、造纸、包装、印刷、烟草、家电、酒和饮料、毛棉纺织、港口码头，铁路、汽车制造、钢铁冶炼、化工和建筑等行业。通常叉车装有两根相同的货叉，它受力大，且要求截面小、重量轻，但作为叉车的重要部件，货叉的质量、性能和在使用过程中的安全性越来越引起人们的关注。目前，货叉在使用过程中仍然会发生断裂事故，且大都发生在焊接部位，属于脆性断裂，给生产和安全都带来了一定的影响。因此，为了提高货叉的质量，需要在设计时对叉车货叉的材料、制造等作出进一步改性。
技术实现思路
本专利技术的目的是针对现有技术中存在的上述问题，提出了一种高韧性叉车货叉。本专利技术的目的可通过如下方案来实现：一种高韧性叉车货叉，所述叉车货叉由钢材材料制成，所述钢材材料包括如下重量...
【技术保护点】
一种高韧性叉车货叉，其特征在于，所述叉车货叉由钢材材料制成，所述钢材材料包括如下重量百分比的成分：C：0.30‑0.35％，Si:0.15‑0.35％,Mn:1.10‑1.40％，Cr：0.02‑0.04％，Ti：001‑0.03％，B：0.002‑0.004％，Ta：0.1‑0.2％，N：0.01‑0.03％，Al2O3晶须：0.1‑0.2％，P:≤0.03％，S：≤0.03％。
【技术特征摘要】
1.一种高韧性叉车货叉，其特征在于，所述叉车货叉由钢材材料制成，所述钢材材料包括如下重量百分比的成分：C：0.30-0.35％，Si:0.15-0.35％,Mn:1.10-1.40％，Cr：0.02-0.04％，Ti：001-0.03％，B：0.002-0.004％，Ta：0.1-0.2％，N：0.01-0.03％，Al2O3晶须：0.1-0.2％，P:≤0.03％，S：≤0.03％。2.根据权利要求1所述的一种高韧性叉车货叉，其特征在于，所述Al2O3晶须的直径为30-50nm。3.一种如权利要求1或2所述的高韧性叉车货叉的制备方法，其特征在于，所述制备方法主要包括以下步骤：称取原料制备成四方柱形并按工艺要求长度切断长条型钢材，并切削出所需要的各斜面，斜度为12-15°；将切削完...