The invention discloses a processing method of glass ornaments, which relates to a processing technology of a glass product. The clear glass rod melting, die press molding; semi-finished products in the surface molding paste and glass rod pigment in different colors, and then burn in the cap in the top flat; semi-finished products covered on the surface of a colored glass to melt on the lamp cap; cut molding; mold half finished surface made of smooth type. The product made by the process of the invention is a product with different colors of pigments sandwiched between two layers of glass, which not only has the beauty of personality, but also has a durable color resistance and abrasion resistance.
【技术实现步骤摘要】
一种玻璃饰品的加工方法
本专利技术涉及一种玻璃产品的加工工艺。
技术介绍
玻璃工艺品可作为装饰品，也可作为日用品。但现有玻璃饰品较单一，也没有个性。
技术实现思路
本专利技术目的在于专利技术一种可表达产品个性的玻璃饰品的加工方法。本专利技术包括以下步骤：1)将明料玻璃棒在1200±20℃的高温灯头上熔化，用模具将其压成型；2)在成型的半成品表面贴与玻璃棒不同颜色的色料，然后在灯头上边烧边压平；3)在半成品表面上覆盖另一有色玻璃，继续在灯头上烧熔；4)用剪刀剪成型；5)用模具将半成品表面制成光滑；6)定型。通过本专利技术工艺制成的产品，是一种在两层玻璃之间夹合不同颜色的色料的产品，不但具有个性美，而且，夹合在其间的色料具有持久的耐色性、耐磨性。本专利技术所述玻璃棒不同颜色的色料为干花或彩色玻璃屑或玻璃网或金箔或银箔或金沙点。不同色料的应用，或加合应用，可使产品花样更多，表现形式更丰富。具体实施方式主要原料：各种颜色实心玻璃棒、金箔或银箔、干花或彩色玻璃屑或玻璃网或金沙点。玻璃网可预先用玻璃丝拉成网状，定型后待用。工艺流程：1)将明料玻璃棒在1200±20℃的高温灯头上熔化，用模具将其压成长方形片状。2)在长方形片状的半成品表面贴与玻璃棒不同颜色的干花或彩色玻璃屑或金沙点或玻璃网至少一种，然后在灯头上边烧边压平。3)在压平的半成的外表面贴合金箔或银箔，继续在灯头上加热，待完全熔合后用模具压平。4)在表面上覆盖透明同形的另一有色玻璃，继续在灯头上烧熔。5)用剪刀剪成树叶状或花瓣状。6)用模具将树叶状或花瓣状半成品表面制成光滑。7)置于保温材料中冷却定型。
【技术保护点】
一种玻璃饰品的加工方法，其特征在于包括以下步 骤： 1)将明料玻璃棒在1200±20℃的高温灯头上熔化，用 模具将其压成型； 2)在成型的半成品表面贴与玻璃棒不同颜色的色料， 然后在灯头上边烧边压平； 3)在半成品表面上覆盖另一有色玻璃，继续在灯头上 烧熔； 4)用剪刀剪成型； 5)用模具将半成品表面制成光滑； 6)定型。
【技术特征摘要】
1.一种玻璃饰品的加工方法，其特征在于包括以下步骤：1)将明料玻璃棒在1200±20℃的高温灯头上熔化，用模具将其压成型；2)在成型的半成品表面贴与玻璃棒不同颜色的色料，然后在灯头上边烧边压平；3)在半成品表面上覆盖...