钛氧化物结晶体、包含钛氧化物结晶体的蓄电设备用电极制造技术

本发明专利技术提供一种无需导电助剂、或者可将导电助剂抑制为最低限度的新颖的钛氧化物结晶体及用途。新颖的钛氧化物结晶体1在表面的一部分具有马格涅利相1a。构成晶体1的钛氧化物是由通式TinO2n表示的氧化钛、由通式MαTiβOγ表示的钛酸化合物。M是金属。马格涅利相1a是由通式TinO2n‑1(3≤n≤10)表示的钛氧化物。所述钛氧化物结晶体1兼具马格涅利相1a的特定而无损作为母材的钛氧化物的特性。

Electrode for electrical storage equipment with titanium oxide crystals and titanium oxide crystals

The present invention provides a novel titanium oxide crystal and a new type of titanium oxide crystal without a conductive additive or a conductive agent to be suppressed to a minimum. The novel titanium oxide crystal 1 has the Magna - N phase 1a in a part of the surface. The titanium oxide, which is composed of crystal 1, is a titanic compound expressed by the general type TinO2n and expressed by the general type M alpha Ti beta O gamma. M is metal. Marg Nelsyan 1a is represented by the general formula TinO2n 1 (n = 3 ~ 10) said the titanium oxide. The titanium oxide crystallizer 1 has a specific and nondestructive properties of the titanium oxide as the parent material of the Marg Nelsyan 1a.

【技术实现步骤摘要】
【国外来华专利技术】钛氧化物结晶体、包含钛氧化物结晶体的蓄电设备用电极
本专利技术涉及一种钛氧化物结晶体。
技术介绍
由通式TinO2n表示的氧化钛、及由通式LiαTiβOγ表示的钛酸锂之类的钛氧化物因钛氧化物的特性而期待在各种用途中的利用。例如，期待将氧化钛(IV)用于色素增感太阳电池的电极、可利用光进行充电的蓄电池、用于利用水分解来制造氢的光电极、颜料、着色料、光催化剂、抗菌原材料、水处理技术、癌症治疗等。期待将钛酸锂用于蓄电池或电容器等蓄电设备的电极活性物质。然而，这些钛氧化物也存在例如电传导性低、或只能吸收紫外线等缺点。因此，也正在研究兼具钛氧化物的特性与其他物质的特性、且弥补钛氧化物的缺点的复合体。例如正在大量进行如下研究：对于氧化钛或钛酸锂，将电传导性高的碳用作导电助剂(例如参照专利文献1)。该研究在锂离子二次电池、或锂离子电容器等蓄电设备中尤其活跃，所述锂离子二次电池的正极及负极分别使用金属化合物粒子，所述锂离子电容器的正极使用活性炭、且负极使用能够可逆地吸附/脱附锂离子的材料(石墨烯或金属化合物等)。原因在于：这些蓄电设备用作移动电话或笔记本电脑等信息装置的电源，而且用于车载等中的再生能本文档来自技高网...

【技术保护点】
一种钛氧化物结晶体，其特征在于：在钛氧化物的结晶表面的一部分具有马格涅利相。

【技术特征摘要】
【国外来华专利技术】2015.03.31 JP 2015-0742671.一种钛氧化物结晶体，其特征在于：在钛氧化物的结晶表面的一部分具有马格涅利相。2.根据权利要求1所述的钛氧化物结晶体，其特征在于：所述钛氧化物是由通式LiαTiβOγ表示的钛酸锂。3.根据权利要求2所述的钛氧化物结晶体，其特征在于：所述钛氧化物是由Li4Ti5O12表示的尖晶石型的钛酸锂。4.根据权利要求1至3中任一项所述的钛氧化物结晶体，其特征在于...

【专利技术属性】
技术研发人员：直井胜彦，直井和子，爪田覚，石本修一，玉光贤次，
申请(专利权)人：日本贵弥功株式会社，
类型：发明
国别省市：日本,JP