The invention provides a complex of wear-resistant rings with excellent thermal conductivity. The iron base sintered body is used to make aluminum alloy wear ring in the hollow hole, which is made of aluminum alloy cast ladle wear ring. The wear ring with the iron-based sintered body, composed by quality% containing C:0.4% ~ 1.5%, Cu:20% ~ 40%, with volume rate of empty hole rate is 15% ~ 50%, the empty hole continuously, pearlite matrix, dispersed in the matrix in the free Cu phase, or dispersed and dispersed particles. Therefore, the wear-resistant ring composite with excellent thermal conductivity has a thermal conductivity of over 40W/m/K and excellent heat dissipation. The strength of the ring is 300MPa, and the linear expansion coefficient is 13.6 to 16.9 x 10.
【技术实现步骤摘要】
【国外来华专利技术】导热性优异的耐磨环用复合体
本专利技术涉及一种汽车等内燃机中所使用的适合用作为耐磨环的铁基烧结体，尤其涉及一种将耐磨环用铁基烧结体铸包在铝合金中而成的耐磨环用复合体。
技术介绍
近年来，就保护地球环境这一观点而言，强烈期望提高汽车等的燃料效率。因此种期望，引擎的轻量化得到发展，铝合金制引擎正在普及。但是，与先前的铸铁相比，铝合金的耐磨耗性低，对于铝合金制引擎，特别是在高温下滑动的滑动部而言，要求提升耐磨耗性。针对此种问题，自先前以来，使用将包含强度高于铝合金(活塞材料)的材料的耐磨环铸包在活塞环槽部中，并利用该耐磨环支撑活塞环的结构的铝制活塞。作为铸包在此种铝制活塞中的耐磨环，通常为经镀铝处理(铝翅处理(Al-Finprocess)等)的高镍耐热铸铁(Ni-resistcastiron)制耐磨环。利用铝合金铸包经铝翅处理的耐磨环，由此可提升耐磨环与铝合金的粘接强度。最近，作为成为铝合金制构件的强化材(耐磨环)的高强度的材料，提出使用多孔质金属烧结体来代替高镍耐热铸铁。例如，在专利文献1中提出有如下的金属烧结体复合材料，其包括：具备具有气孔的三维晶格结构的铁系的多孔...
【技术保护点】
一种导热性优异的耐磨环用复合体，其是利用铝合金铸包耐磨环用铁基烧结体而成的耐磨环用复合体，其特征在于：所述耐磨环用铁基烧结体是具有如下的组成与组织的铁基烧结体，所述组成以质量％计含有C：0.4％～1.5％、Cu：20％～40％，并且剩余部分包含Fe及不可避免的杂质，所述组织以体积率计空孔率为15％～50％，空孔连续地存在，基体为珠光体，在所述基体中分散有游离Cu相，且铝合金含浸在所述空孔内，导热率为40W/m/K以上，压环强度为300MPa以上。
【技术特征摘要】
【国外来华专利技术】2015.07.01 JP 2015-1328431.一种导热性优异的耐磨环用复合体，其是利用铝合金铸包耐磨环用铁基烧结体而成的耐磨环用复合体，其特征在于：所述耐磨环用铁基烧结体是具有如下的组成与组织的铁基烧结体，所述组成以质量％计含有C：0.4％～1.5％、Cu：20％～40％，并且剩余部分包含Fe及不可避免的杂质，所述组织以体积率计空孔率为15％～50％，空孔连续地存在，基体为珠光体，在所述基体中分散有游离Cu相，且铝合金含浸在所述空孔内，导热率为40W/m...