The invention discloses a method for preparing calcium silicate slag cementitious material, made of the alkali activated cementitious materials containing the following components and raw materials in parts by weight: 200 to 400 portions of calcium silicate slag, industrial water glass is 20 ~ 40, 200 ~ 300 rotary kiln clinker 50 ~ 100, gypsum and zeolite powder 50 ~ 100, 30 ~ 60 pyrophyllite. It has improved the performance of early strength, high temperature resistance, acid corrosion resistance and consolidation of metal ions, reduced the production cost, and opened up a new way in resource utilization of silicon calcium slag, which has significant environmental and economic benefits.
【技术实现步骤摘要】
一种硅钙渣制备的碱激发胶凝材料
本专利技术涉及一种硅钙渣制备的碱激发胶凝材料，属于水泥制造
技术介绍
我国内蒙古等地区出产高铝粉煤灰，其铝含量高达40％～60％。为充分利用此种铝矿资源，目前国内大多采用石灰石烧结法对其进行铝处理。硅钙渣是粉煤灰提取氧化铝后的残渣，其主要成分为硅酸二钙。由于提铝过程中都会有部分碱液残留在残渣(硅钙渣)中，硅钙渣碱含量一般为3％～8％。这位硅钙渣的资源化处理带来了极大的不便。对于硅钙渣的资源化利用，现有技术中利用其生产碱激发胶凝材料的研究比较多。但是由于硅钙渣中碱含量较高，无法直接用于水泥生产，因此将硅钙渣用作水泥生产原料时，必须进行脱碱处理。此外，为保证硅酸三钙含量，以硅钙渣为原料生产熟料过程中还需添加石灰石等其他组分，水泥生产的成本及能耗较高。以粉煤灰、矿渣制备碱激发胶凝材料的成果比较多，但是用硅钙渣制备碱激发胶凝材料的技术还很稀缺。
技术实现思路
针对上述现有技术存在的问题，本专利技术提供一种硅钙渣制备的碱激发胶凝材料，提高了在早期强度、耐高温、耐酸腐蚀、固结金属离子方面的性能，降低了生产成本，且在硅钙渣的资源化利用方面开辟了新的途径，具有显著的环保及经济效益。为了实现上述目的，本专利技术采用的技术方案是：一种硅钙渣制备的碱激发胶凝材料，所述的碱激发胶凝材料含有下述组分及重量份数的原料制成的：硅钙渣200份～400份，工业级液体水玻璃20份～40份，旋窑熟料200份～300份，石膏50份～100份，沸石粉50份～100份，叶腊石30份～60份。进一步，每1Kg所述的硅钙渣的矿物成分按重量份数为β型硅酸二钙450份～...
【技术保护点】
一种硅钙渣制备的碱激发胶凝材料，其特征在于，所述的碱激发胶凝材料含有下述组分及重量份数的原料制成的：硅钙渣200份～400份，工业级液体水玻璃20份～40份，旋窑熟料200份～300份，石膏50份～100份，沸石粉50份～100份，叶腊石30份～60份。
【技术特征摘要】
1.一种硅钙渣制备的碱激发胶凝材料，其特征在于，所述的碱激发胶凝材料含有下述组分及重量份数的原料制成的：硅钙渣200份～400份，工业级液体水玻璃20份～40份，旋窑熟料200份～300份，石膏50份～100份，沸石粉50份～100份，叶腊石30份～60份。2.根据权利要求1所述的一种硅钙渣制备的碱激发胶凝材料，其特征在于，每1Kg所述的硅钙渣的矿物成分按重量份数为β型硅酸二钙450份～650份，水化钙铝榴石150份～200份，方解石100份～150份和水合铝酸三钙50份～100份。3.根据权利要求1所述的一种硅钙渣制备的碱激发胶凝材料，其特征在于，每1...
【专利技术属性】
技术研发人员：崔松，
申请(专利权)人：江苏兆佳建材科技有限公司，
类型：发明
国别省市：江苏,32