The invention belongs to the technical field of catalysis, relates to a copper based catalyst for CO high temperature shift reaction conditions than for low and high temperature gas steam conversion process, catalyst with copper and zinc and aluminum as the main component, consisting of (WT):CuO30%~45%, ZnO25%~45%, Al2O35%~15%, adding alkali metal promoter Me2O0.5% ~ 5.5%. Prepared by precipitation method, alkali metal oxide (Me2O) is K or Cs, the oxide or oxide hydrate catalyst prepared by precipitation matrix, improve the catalyst at low steam gas ratio high activity conditions and eliminate the high iron catalyst system F T side reaction temperature CO the conversion process of catalyst high conversion rate, CO exports reached about 1%, greatly improving the efficiency of heat exchange process, significantly reduce the energy consumption of ammonia and hydrogen production processes.
【技术实现步骤摘要】
一种铜基一氧化碳高温变换催化剂
本专利技术属于催化
，涉及一种一氧化碳和水蒸汽在低汽气比（相当于转化炉水碳比2.75以下）条件下进行高温变换反应的催化剂及其制备方法，用于合成氨厂和制氢装置，特别适用于节能型氨厂的低汽气比高温变换反应以降低合成氨或制氢工艺的有耗。
技术介绍
通常，合成氨和制氢工艺都涉及进行变换反应，通常包括一步或两步工艺，即在300℃以上的高温变换和低温变换。高温变换催化剂通常由活性组分Fe2O3与其它助剂化合物组成，有的还含有铬氧化物助剂，铬的氧化物是一种毒性物质，在生产的使用过程中，容易生成人身伤害，因此属于避免使用的物质。同时，由于Fe3O4在使用过程中容易形成金属铁和碳化铁，在高温变换条件下对CO甲烷化和F—T合成反应有催化作用，致使H2产率下降。为了控制副反应的发生，需使用更多的蒸汽，从而增加能耗。随着合成氨工业的节能化、大型化以及制氢行业的高效率，适用于低水碳比的节能型催化剂越来越受到普遍重视，尤其在催化剂的选择性方面还不能适应当今日益提高的环保要求。如专利CN1140630A提供的一种低水碳比的高温变换催化剂及其制备方法，也是为...
【技术保护点】
一种一氧化碳高温变换催化剂，其特征在于该催化剂为不含铁铬的铜‑锌‑铝系催化剂，并且添加了碱金属助剂。
【技术特征摘要】
1.一种一氧化碳高温变换催化剂，其特征在于该催化剂为不含铁铬的铜-锌-铝系催化剂，并且添加了碱金属助剂。2.如权利要求1所述催化剂各组分的重量组成为：CuO30%~45%，ZnO25%~45%，Al2O35%~15%，碱金属元素氧化物Me2O重量含量为0.5%～5.5%，Me为K、Cs中的一种或者一种以上的混合物，余为成型助剂。3.如权利要求1、2所述催化剂的制备方法，其特征在于采用沉淀法制备，首先将铜锌的可溶性盐用水溶性碱溶液进行沉淀得到铜锌的微溶或不溶化合物，...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。