The invention provides a composite aerated concrete and a production process, which relates to a technical field of concrete material. The invention comprises the weight of raw materials prepared by the 20 cement 30, lime 30 40 copies, 70 copies, 50 sand fly ash 50 60 copies, 15 copies, 10 slag huanmingfen 5 10 copies, 5 copies, 1 sodium carbonate filling agent 8 20 0.1, 0.5 copies of admixture. The invention has the advantages of good sound insulation, heat insulation performance, environmental performance and light weight, heat etc., to reduce the structural section, reduce the amount of steel structure is strong, especially for high-rise building, environmental protection and energy saving, light weight, good insulation, processing and flame, emphasized by the market.
【技术实现步骤摘要】
一种复合型加气混凝土及其生产工艺
本专利技术涉及一种混凝土材料
，特别是涉及一种复合型加气混凝土及其生产工艺。
技术介绍
复合型加气混凝土是一种轻质多孔的新型墙体材料，可以制作成墙体砌块、墙板、楼板、屋面板、保温板和保温管等制品。目前复合型加气混凝土在我国已广泛应用于工业与民用建筑，作为承重或非承重的结构材料和围护保温材料，成为新型墙体材料的一个重要组成部分。
技术实现思路
针对上述问题中存在的不足之处，本专利技术提供一种复合型加气混凝土及其生产工艺，使其具有良好的隔音、隔热性能、环保性能和体轻、抗热等优点，对减少结构断面、降低结构含钢量大为有力，特别有利于高层建筑，环保节能、质量轻、保温好、可加工和不燃烧等优点，受到市场的普遍重视。为了解决上述问题，本专利技术提供一种复合型加气混凝土，其中，由包含下述重量份的原料制备而成：水泥60-80份、生石灰40-60份、砂子50-70份、矿渣10-20份、元明粉5-10份、碳酸钠1-10份、铝粉5-10份。优选的，由包含下述重量份的原料制备而成：水泥60-80份、生石灰40-60份、砂子50-70份、矿渣10-20份、元...
【技术保护点】
一种复合型加气混凝土，其特征在于，由包含下述重量份的原料制备而成：水泥60‑80份、生石灰40‑60份、砂子50‑70份、矿渣10‑20份、元明粉5‑10份、碳酸钠1‑10份、铝粉5‑10份。
【技术特征摘要】
1.一种复合型加气混凝土，其特征在于，由包含下述重量份的原料制备而成：水泥60-80份、生石灰40-60份、砂子50-70份、矿渣10-20份、元明粉5-10份、碳酸钠1-10份、铝粉5-10份。2.如权利要求1所述的复合型加气混凝土，其特征在于，由包含下述重量份的原料制备而成：水泥60-80份、生石灰40-60份、砂子50-70份、矿渣10-20份、元明粉5-10份、碳酸钠1-10份、铝粉5-10份。3.如权利要求2所述的复合型加气混凝土，其特征在于，由包含下述重量份的原料制备而成：水泥...
【专利技术属性】
技术研发人员：崔岩成，
申请(专利权)人：辽阳市秦甄环保建材有限公司，
类型：发明
国别省市：辽宁,21