The invention belongs to the field of building materials, put forward a kind of combustion performance of a thermal insulation mortar, is prepared from the following raw materials: weight ratio of fly ash cement 40 stones 20 50 copies, 30 copies, 40 copies of EVB tap water 30, 10 insulation particles 20, nano powder 1 into 5 copies. Assistant of film 1 3; EVB insulation particle size in 50 mm or less; nano magnesium powder particle diameter less than 100um; film-forming agent is polyethylene glycol propylene glycol ether; to maintain the original thermal insulation mortar thermal insulation performance; combustion performance can reach a level that is better than the ordinary thermal insulation mortar, reduce live in safety.
【技术实现步骤摘要】
一种燃烧性能为A级的保温砂浆
本专利技术属于建筑材料领域，具体涉及一种燃烧性能为A级的保温砂浆。
技术介绍
自2004年之后，国家对建筑执行强制节能设计，保温砂浆作为主流的墙体保温材料得到广泛的推广，为建设资源节约型社会做出了巨大贡献。但是，普通保温砂浆因保温性能不达标，极易造成火灾隐患，上海静安区外墙节能改造引发的火灾给我们敲墙了警钟，如何在保证保温砂浆保温性能的同时还能提高砂浆的防火性能，是个值得我们深思的问题。
技术实现思路
：本专利技术的目的在于克服现有保温砂浆的缺陷，提供一种燃烧性能为A级的保温砂浆。技术方案：为实现上述专利技术目的，本专利技术提供了以下技术方案：1．一种燃烧性能为A级的保温砂浆，是由以下重量份比的原料制成：粉煤灰水泥40-50份，石子20-30份，自来水30-40份，EVB保温颗粒10-20份，纳米镁粉1-5份，成膜助剂1-3份。2．所述的EVB保温颗粒粒径在50㎜以内。3．所述的纳米镁粉粒径在100um以内。4．所述的成膜助剂是聚乙二醇丙二醇醚。本专利技术的有益效果在于：1．在普通EVB保温砂浆的基础上进行改良，保持了原有保温砂浆的保温性能。2．燃烧性能可达A级，优于普通保温砂浆，减少活在安全隐患。具体实施方式为了使本专利技术实现的技术手段、创作特征、达成目的与功效易于明白易懂，下面结合具体实施例对本专利技术进一步详细说明，但本专利技术的内容完全不局限于此。实施例1：1．一种燃烧性能为A级的保温砂浆，是由以下重量的原料制成：粉煤灰水泥40Kg，石子20Kg，自来水40Kg，EVB保温颗粒10Kg，纳米镁粉5Kg，成膜助剂1Kg。2...
【技术保护点】
一种燃烧性能为A级的保温砂浆，其特征在于，是由以下重量份比的原料制成：粉煤灰水泥40‑50份，石子20‑30份，自来水30‑40份，EVB保温颗粒10‑20份，纳米镁粉1‑5份，成膜助剂1‑3份。
【技术特征摘要】
1.一种燃烧性能为A级的保温砂浆，其特征在于，是由以下重量份比的原料制成：粉煤灰水泥40-50份，石子20-30份，自来水30-40份，EVB保温颗粒10-20份，纳米镁粉1-5份，成膜助剂1-3份。2.根据权利要求1所述的一种燃烧性能为A级的保温砂浆...