The invention discloses a color quartz sand permeable bricks, the permeable brick by weight, which comprises the following components: quartz sand 30 50, cement 30 50, water 50 80 copies, 10 copies, 5 colorant magnesium aluminium agent 5 10, 20 fine basalt stone 30, cenosphere 10 15, accelerating 3 5 copies, 10 copies of 5 powder. The utility model has the advantages of magnesium aluminium agent according to the invention, no organic binder, exist in the heating process due to oxidation caused high temperature strength is low, the water permeable brick with good temperature resistant performance; the invention solves the traditional process of using permeable brick brick brick surface easily weathered, fall off, influence beautiful, and because of the brick layer, low permeability, waterproof effect is not good problem.
【技术实现步骤摘要】
一种石英砂彩色透水砖
本专利技术建筑
,具体涉及一种石英砂彩色透水砖。
技术介绍
随着城市化建设的开展,城市中铺设越来越多的硬质地面,其环保功能差,不宜人居。例如,混凝土地面的热岛效应、排水性差引起的地面积水和城市内涝、自然降水无法渗透补充地下水导致地下水循环遭破坏等。现有的混凝土路面砖是一种典型的硬质地面,大多为实心砖,透水系数很低,基本不具备透水功能。海绵城市即城市能够像海绵一样,在适应环境变化和应对自然灾害等方面具有良好的“弹性”,下雨时能吸水、储水、渗水、净水,需要用水时,储存的水能“释放”并加以利用,能够提升城市生态系统和减少城市洪涝灾害的发生。现有技术中,透水砖已经是市场上常见的建筑材料,但是现有透水砖大部分存在砖体易风化,砖面脱落,影响美观,并且很多砖由于分层问题,导致渗透率低,透水效果不好。
技术实现思路
本专利技术的目的在于针对现有技术的不足,现提供一种透水性能好、耐磨性能好的石英砂彩色透水砖。为解决上述技术问题,本专利技术采用的技术方案为:一种石英砂彩色透水砖,其创新点在于:所述透水砖按重量份计,包括如下组分:石英砂30-50份、水泥30-50份、水50-80份、着色剂5-10份、镁铝胶结剂5-10份、玄武岩细石20-30份、空心微珠10-15份、速凝剂3-5份、石粉5-10份。进一步的,所述石英砂粒径为100nm-1000nm。进一步的,所述玄武岩细石粒径为1mm-2mm。本专利技术的有益效果如下:本专利技术采用镁铝胶结剂,不存在有机胶结剂,在加热过程中存在的因氧化导致的耐温强度低的问题,使透水砖耐温性能好;本专利技术解决了传统透水 ...
【技术保护点】
一种石英砂彩色透水砖,其特征在于:所述透水砖按重量份计,包括如下组分:石英砂30‑50份、水泥30‑50份、水50‑80份、着色剂5‑10份、镁铝胶结剂5‑10份、玄武岩细石20‑30份、空心微珠10‑15份 、速凝剂3‑5份、石粉5‑10份。
【技术特征摘要】
1.一种石英砂彩色透水砖,其特征在于:所述透水砖按重量份计,包括如下组分:石英砂30-50份、水泥30-50份、水50-80份、着色剂5-10份、镁铝胶结剂5-10份、玄武岩细石20-30份、空心微珠10-15份、速凝剂...