The invention provides a chrome sand permeable brick, which relates to the field of building materials. A chrome sand permeable brick, which is composed of the following raw materials by weight ratio: 1 water 20, chromium 10 sand cement 10 95 copies, 30 copies, 20 copies of powder 1, 0.01 10 colorants. The invention has simple formula, simple technological process and easy popularization. The perfect solution to the traditional process of using permeable brick brick brick surface easily weathered, fall off, affecting the appearance, and a lot of permeable bricks due to delamination problems, resulting in low permeability, influence the permeability effect of the problem, and the forming method of the invention adopts extrusion molding, without burning, low energy consumption, energy saving and emission reduction.
【技术实现步骤摘要】
一种铬沙透水砖
本专利技术涉及建筑材料领域,尤其指一种铬沙透水砖。
技术介绍
海绵城市的概念在2012年首次提出,海绵城市,即城市能够像海绵一样,在适应环境变化和应对自然灾害等方面具有良好的“弹性”,下雨时吸水、蓄水、渗水、净水,需要时将蓄存的水“释放”并加以利用。提升城市生态系统功能和减少城市洪涝灾害的发生。海绵城市建设的最重要的措施之一就是城市地面的透水铺装,以达到将自然降水最大限度的留存在城市内部,便于循环利用的目的。而城市的透水铺装过程中,透水砖是最重要的建筑材料之一。现有技术中,透水砖已经是市场上常见的建筑材料,提供透水砖的企业也不胜枚举。但是,市场上现有的透水砖大部分存在砖体易风化,砖面脱落,影响美观,并且很多透水砖由于分层问题,导致透水率低,影响透水效果。本申请专利技术人经过多次研究实验,提供一种铬沙透水砖,能够很好地解决上述问题。。
技术实现思路
为了解决上述技术问题,本专利技术提供一种铬沙透水砖。本专利技术解决其技术问题所采用的技术方案是:一种铬沙透水砖,由以下原料按重量份数组成:水1-20份,铬沙10-95份,水泥10-30份,石粉1-20份,着色剂0.01-10份。优选的,一种铬沙透水砖,由以下原料按重量份数组成:水5-10份,铬沙30-80份,水泥15-25份,石粉5-15份,着色剂1-8份。优选的,一种铬沙透水砖,由以下原料按重量份数组成:水6-8份,铬沙40-70份,水泥16-22份,石粉8-12份,着色剂3-7份。优选的,一种铬沙透水砖,由以下原料按重量份数组成:水10份,铬沙52份,水泥20份,石粉11份,着色剂2份。一种铬沙透 ...
【技术保护点】
一种铬沙透水砖,其特征在于:由以下原料按重量份数组成:水1‑20份,铬沙10‑95份,水泥10‑30份,石粉1‑20份,着色剂0.01‑10份。
【技术特征摘要】
1.一种铬沙透水砖,其特征在于:由以下原料按重量份数组成:水1-20份,铬沙10-95份,水泥10-30份,石粉1-20份,着色剂0.01-10份。2.根据权利要求1所述的一种铬沙透水砖,其特征在于:由以下原料按重量份数组成:水5-10份,铬沙30-80份,水泥15-25份,石粉5-15份,着色剂1-8份。3.根据权利要求1所述的一种铬沙透水砖,其特征在于:由以下原料按重量份数组成:水6-8份,铬沙40-70份,水泥16-22份,石粉8-12份,着色剂3-7份。4.根据...