The invention belongs to the field of building materials, put forward a kind of nano magnesium inorganic thermal insulation mortar is made by weight ratio of raw materials: Ordinary portland cement 40 50 copies, 15 copies, 10 light calcium powder EVB insulation particles 10 15 copies, 10 copies, 5 nanometer magnesium crack fiber 5 1 1, coalescents 2; the nano magnesium powder particle diameter less than 60um; the crack fiber polypropylene fiber crack; the film-forming agent is alcohol ester twelve coalescents; improve the linear shrinkage rate of the original mortar, the cracking resistance has been greatly enhanced; waterproof mortar can enhance the performance of.
【技术实现步骤摘要】
一种添加纳米镁粉的无机保温砂浆
本专利技术属于建筑材料领域,具体涉及一种添加纳米镁粉的无机保温砂浆。
技术介绍
作为无机保温砂浆的代表,EVB保温砂浆因其性能稳定,保温效果良好而被广泛应用于建筑外墙保温工程。但限于EVB保温颗粒骨料自身性能特点,此类无机保温砂浆还存在抗裂性差、易开裂起鼓且强度不高等问题,故其适用范围受一定限制。
技术实现思路
本专利技术的目的在于针对现有技术的不足,提供一种添加纳米镁粉的无机保温砂浆。技术方案1.一种添加纳米镁粉的无机保温砂浆,是由以下重量份比的原料制成:普通硅酸盐水泥40-50份、轻钙粉10-15份、EVB保温颗粒10-15份、纳米镁粉5-10份、抗裂纤维1-5份,成膜助剂1-2份。2.所述的纳米镁粉粒径在60um以内。3.所述的抗裂纤维是聚丙烯抗裂纤维。4.所述的成膜助剂是醇酯十二成膜助剂。本专利技术的有益效果在于:1.添加了纳米镁粉及抗裂纤维,提高了原有砂浆的线性收缩率,使其抗裂性得到极大的增强。2.添加了成膜助剂,砂浆防水性能得到加强。具体实施方式为了使本专利技术实现的技术手段、创作特征、达成目的与功效易于明白易懂,下面结合具体实施例对本专利技术进一步详细说明,但本专利技术的内容完全不局限于此。实施例1:1.一种添加纳米镁粉的无机保温砂浆,是由以下重量的原料制成:普通硅酸盐水泥40Kg、轻钙粉10Kg、EVB保温颗粒10Kg、纳米镁粉7Kg、抗裂纤维3Kg,成膜助剂1Kg。2.所述的纳米镁粉粒径为60um。3.所述的抗裂纤维是聚丙烯抗裂纤维。4.所述的成膜助剂是醇酯十二成膜助剂。实施例2:1.一种添加纳米镁粉的无机保温 ...
【技术保护点】
一种添加纳米镁粉的无机保温砂浆,其特征在于,是由以下重量份比的原料制成:普通硅酸盐水泥40‑50份、轻钙粉10‑15份、EVB保温颗粒10‑15份、纳米镁粉5‑10份、抗裂纤维1‑5份,成膜助剂1‑2份。
【技术特征摘要】
1.一种添加纳米镁粉的无机保温砂浆,其特征在于,是由以下重量份比的原料制成:普通硅酸盐水泥40-50份、轻钙粉10-15份、EVB保温颗粒10-15份、纳米镁粉5-10份、抗裂纤维1-5份,成膜助剂1-2份。2.根据权利要求1所述的一种添加纳米镁粉的无机保...