The invention relates to a method and an alumina composite graphene carrier catalyst for hydrogenation of aromatics production n-heptane solvent oil first, the raffinate oil and n-heptane solvent oil according to the volume ratio of 3 ~ 5.0:1.0 mixing ratio, static balance; then, mixed oil in the hydrogenation catalyst under the effect of heating on in the environment of hydrodearomatics, operating temperature is 120 to 180 DEG C, working pressure is 2 ~ 3.0MPa, hydrogen oil volume ratio of 120 to 300; the hydrogenation catalyst by metal carrier and active components, the carrier is made of alumina and graphene; finally, separating system of hydrogen separation product of distillation, the initial boiling point of 95 DEG C, 98% distillate amount of not more than 100 DEG C. The N - heptane solvent oil obtained by this application has lower impurity content and higher material quality.
【技术实现步骤摘要】
一种氧化铝复合石墨烯载体加氢催化剂脱芳烃生产正庚烷溶剂油的方法
本专利技术属于加氢脱芳烃生产溶剂油的方法，具体涉及一种采用加氢催化剂脱芳烃生产正庚烷溶剂油的方法。
技术介绍
烃类溶剂油是溶剂油重要的分支，溶剂油的性质视其用途不同而有别，选择溶剂油应主要考虑其溶解性、挥发性、安全性。当然，根据其用途不同，其它的各项性能也不能忽略，有时甚至更重要。溶剂油包括切取馏分和精制两个过程。切取馏分过程通常有以下三种途径：由常压塔直接切取；将相应的轻质直馏馏分再切割成适当的窄馏分；和将催化重整抽余油进行分馏。各种溶剂油馏分一般都需要经过精制加工。以改善色泽，提高安定性，除去腐蚀性物质和降低毒性等。
技术实现思路
本专利技术的目的是提供一种脱芳烃生产正庚烷溶剂油的方法，在抽余油中预先添加部分正庚烷溶剂油，然后进行后续脱芳烃生产，提高正庚烷溶剂油的回收效率，降低杂质含量，获得更好的溶剂油品质。本专利技术解决上述问题所采用的技术方案为：一种氧化铝复合石墨烯载体加氢催化剂脱芳烃生产正庚烷溶剂油的方法，包括如下步骤：（1）将抽余油和正庚烷溶剂油按体积比为3.0～5.0:1.0的比例混合，静置...
【技术保护点】
一种氧化铝复合石墨烯载体加氢催化剂脱芳烃生产正庚烷溶剂油的方法，其特征在于：包括如下步骤：（1）将抽余油和正庚烷溶剂油按体积比为3.0～5.0:1.0的比例混合，静置平衡；（2）混合油分在加氢催化剂的作用下，于加热环境中加氢脱芳烃，作业温度为120～180℃，作业压力为2.0～3.0MPa，氢油体积比120～300；所述加氢催化剂由载体和金属活性组分构成，该载体由氧化铝和石墨烯组成；（3）分离去除体系中的氢气，对产物精馏分离，初馏点为95℃，98%馏出量不大于100℃。
【技术特征摘要】
1.一种氧化铝复合石墨烯载体加氢催化剂脱芳烃生产正庚烷溶剂油的方法，其特征在于：包括如下步骤：（1）将抽余油和正庚烷溶剂油按体积比为3.0～5.0:1.0的比例混合，静置平衡；（2）混合油分在加氢催化剂的作用下，于加热环境中加氢脱芳烃，作业温度为120～180℃，作业压力为2.0～3.0MPa，氢油体积比120～300；所述加氢催化剂由载体和金属活性组分构成，该载体由氧化铝和石墨烯组成...