The invention discloses a cadmium selenide bismuth tungstate composite photocatalyst preparation method comprises the following steps: (1), cadmium chloride hydrate, 3 mercaptopropionic acid according to 1: (1.5 ~ 1.7) molar ratio of dissolved in deionized water, the formation of mixed solution, adjusted pH to 7 ~ 8; adding selenium hydride in the mixed solution of Namibia precursor, in 160 ~ 170 DEG C for 30 to 35 minutes, get CdSe quantum dots; (2), the CdSe quantum dots and bismuth tungstate dissolved in deionized water, at 80 to 90 DEG C reflux for 20 ~ 25 hours, get CdSe centrifugal drying bismuth tungstate composite photocatalyst. Cadmium selenide bismuth tungstate composite photocatalyst of the invention has good catalytic activity and high stability.
【技术实现步骤摘要】
硒化镉-钨酸铋复合光催化剂的制备方法
本申请属于废水处理
，特别是涉及一种硒化镉-钨酸铋复合光催化剂的制备方法。
技术介绍
硒化镉是禁带宽度为1.7eV的直接带隙半导体材料，具有立方闪锌矿和六方纤锌矿两种晶体结构，其中立方相结构为亚稳态，只能存在于较低温度，高温时转变为六方相结构。硒化镉在常温下可同时存在立方和六方两种晶相。硒化镉纳米晶是半导体纳米晶中研究最广泛，应用前景最好的一类II-VI族半导体纳米晶，由于其具有重要的非线性光学性质，发光性质及其他物理化学特性而备受世人的瞩目。作为一种非常重要的半导体材料，已经在各种发光装置，激光与红外探测器件，红外窗口与非线性光学材料和光敏传感器等领域展示了广阔的应用前景。特别是硒化镉能很好地吸收可见光，因而它是光化学催化剂的首选材料。硒化镉极易光腐蚀，光稳定性差，二氧化钛的光吸收阈值局限在紫外光去，太阳利用率低，这些不足极大限制了他们性能的发挥。
技术实现思路
本专利技术的目的在于提供一种硒化镉-钨酸铋复合光催化剂的制备方法，以克服现有技术中的不足。为实现上述目的，本专利技术提供如下技术方案：本申请实施例公开一种硒化镉-...
【技术保护点】
一种硒化镉‑钨酸铋复合光催化剂的制备方法，其特征在于，包括步骤：(1)、将水合氯化镉、3‑巯基丙酸按照1:(1.5～1.7)摩尔比溶解在去离子水中，形成混合溶液，调节溶液pH至7～8；在混合溶液中加入硒氢化纳前驱体，在160～170℃下反应30～35分钟，获得硒化镉量子点；(2)、将硒化镉量子点和钨酸铋溶解在去离子水中，在80～90℃回流20～25小时，离心干燥获得硒化镉‑钨酸铋复合光催化剂。
【技术特征摘要】
1.一种硒化镉-钨酸铋复合光催化剂的制备方法，其特征在于，包括步骤：(1)、将水合氯化镉、3-巯基丙酸按照1:(1.5～1.7)摩尔比溶解在去离子水中，形成混合溶液，调节溶液pH至7～8；在混合溶液中加入硒氢化纳前驱体，在160～170℃下反应30～35分钟，获得硒化镉量子点；(2)、将硒化镉量子点和钨酸铋溶解在去离子水中，在80～90℃回流20～25小时，离心干燥获得硒化镉-钨酸铋复合光催化剂。2.根据权利要求1所述的硒化镉-钨酸铋复合光催化剂的制备方法，其特征在于：步骤(1)中，钨酸铋的制备方法：先按照硝酸铋与硝酸之间的质量比为(3～5)∶1的比例将硝酸铋加入浓度为(1～4)mol/L的硝酸溶液中，得到硝酸铋溶液，再按照钨酸钠与去离子水之间的质量比为(30～50)∶1的比例将钨酸钠加入去离子水中搅拌均匀，得到钨酸钠溶液，接着，先将聚乙烯吡咯烷酮加入钨酸钠溶液中搅...
【专利技术属性】
技术研发人员：沙冰娟，
申请(专利权)人：张家港市金港镇宏业海绵复合厂，
类型：发明
国别省市：江苏,32