The invention discloses a method of reducing the odor of polyether polyol by two - element composite catalyst and photocatalytic oxidation. The method first syntheses polyether polyol with a specific two element composite catalyst, \potassium alcohol potassium and zinc valerate\, and improves the chemical reaction rate. At the same time, during the post-processing of products, TiO2 photocatalytic oxidation of aldehydes is used to reduce the concentration of low molecular aldehydes, so as to reduce the odor of polyether polyols. The polyether polyol prepared by the invention has low content of low molecular aldehydes, such as free formaldehyde and acetaldehyde, and the quality of the product is stable and the use performance is good.
【技术实现步骤摘要】
通过催化剂和光催化氧化协同降低聚醚多元醇气味的方法
本专利技术属于高分子化合物的制备方法,具体地说一种通过二元复合催化剂和光催化氧化协同降低聚醚多元醇气味的方法。
技术介绍
聚醚多元醇在汽车工业中有着广泛应用,比如用于制造聚氨酯高回弹坐垫、方向盘等。随着人们环保意识的日益增强,聚氨酯制品存在的挥发性、高气味等问题已经成为限制其应用的重要因素。国家于2012年3月1日发布了乘用车内空气质量评价指南(GB/T27630—2011),规定车内空气中甲醛、乙醛等挥发醛类物质的含量。从合成原料和工艺过程进行分析,聚醚多元醇产品的气味主要是未反应的氧化丙烯单体,低分子的醛类物质产生的。这不但影响了汽车内饰使用的舒适性,也对人体健康构成危害。因此,找出聚醚多元醇产生气味的原因并加以有效解决,就成为提升产品品质的关键。目前,国内研究人员和相关企业都在不断进行探索。如技术专利(申请号:201220436842.8)“汽提法除聚醚多元醇异味装置”,有减少聚醚多元醇气味的效果;专利技术专利(申请号:201410383509.9)“降低聚醚多元醇含量的方法”,通过加入过氧化氢氧化聚醚多元醇中的挥发性有机物达到改善聚氨酯制品气味的目的。青岛科技大学秦好辉等人报道了“过氧化氢减少聚醚多元醇中挥发性醛类物质的工艺研究”[当代化工,2015,44(1):49-50],他们认为所述工艺:(1)既可以显著去除聚醚多元醇挥发性醛类物质,同时又可以降低聚醚多元醇气味;(2)简单易行,成本低廉,无需设备改造既可以广泛应用于聚醚多元醇批量生产中。上述方法针对的都是对产品进行后处理以降低聚醚多元醇的气 ...
【技术保护点】
一种通过催化剂和光催化氧化协同降低聚醚多元醇气味的方法,其特征在于:以胺类物质作为起始剂,采用二元复合催化剂合成聚醚多元醇,提高化学反应速率;同时,在产品的后处理过程中,采用二氧化钛光催化剂催化氧化醛类物质;上述两步骤协同作用,有效地降低聚醚多元醇中低分子醛类甲醛、乙醛的含量。
【技术特征摘要】
1.一种通过催化剂和光催化氧化协同降低聚醚多元醇气味的方法,其特征在于:以胺类物质作为起始剂,采用二元复合催化剂合成聚醚多元醇,提高化学反应速率;同时,在产品的后处理过程中,采用二氧化钛光催化剂催化氧化醛类物质;上述两步骤协同作用,有效地降低聚醚多元醇中低分子醛类甲醛、乙醛的含量。2.根据权利要求1所述的通过催化剂和光催化氧化协同降低聚醚多元醇气味的方法,其特征在于:二元复合催化剂为...
【专利技术属性】
技术研发人员:翟洪金,应珏,倪小明,郑磊,于文超,王飞,任翠环,
申请(专利权)人:句容宁武新材料股份有限公司,
类型:发明
国别省市:江苏,32