一种硫吸附剂的再生方法技术
A regeneration method of sulfur adsorbents
The invention discloses a regeneration method of sulfur adsorbent, the method comprises: containing nickel component to the adsorbent into the regenerator and the regeneration gas contact and regeneration, regeneration of adsorbent; which is characterized in that the method also includes the regeneration of adsorbent into the regenerator in the receiver after cooling, cooling by adsorbent, adsorbent and the cooling will be part of the students in the coke burning regeneration of adsorbent mixed to the regenerator, another part of the cooling adsorbent for the adsorption reaction into the reactor. The regeneration method of the present invention can reduce the deactivation of the sulfur adsorbent.
【技术实现步骤摘要】
一种硫吸附剂的再生方法
本专利技术涉及一种硫吸附剂的再生方法。
技术介绍
随着人们对环境保护的日益重视，对作为燃料的轻质烃中硫含量的限制也越来越严格。以汽油为例，欧盟在2005年就已经规定硫含量不超过50μg/g，并且于2010年实施的欧Ⅴ汽油标准中规定硫含量小于10μg/g。中国于2013年12月31号开始实施的国Ⅳ标准规定汽油硫含量不大于50μg/g，并计划于2017年初在全国推广实施国Ⅴ标准，届时汽油中的硫含量将不大于10μg/g。近年来，S-Zorb汽油吸附脱硫工艺由于具有脱硫深度高、氢耗低、辛烷值损失少等特点在国内得到了迅速推广。按照美国专利US6274533、US6869522和US7427581等公开的方法，在对催化裂化汽油进行吸附脱硫时，能够将催化裂化汽油中的硫脱除到10微克/克以下，且产物的抗暴指数损失不超过0.6个单位，吸附脱硫的反应条件为：0.1～10.3MPa、37.7～537.7℃、重时空速为0.5～50h-1和临氢条件下。所用吸附剂以氧化锌、硅石和氧化铝混合物为载体，其中氧化锌占10～90重％、硅石占5～85重％、氧化铝占5～30重％。...
【技术保护点】
一种硫吸附剂的再生方法，该方法包括：将含有镍组分的待生吸附剂送入再生器中与烧焦再生气体接触并进行烧焦再生，得到再生吸附剂；其特征在于，该方法还包括：将所得再生吸附剂送入再生器接收器中进行降温处理后，得到降温吸附剂，将部分所得降温吸附剂与所述待生吸附剂混合送入再生器中进行所述烧焦再生，将另一部分所得降温吸附剂用于送入反应器中进行吸附反应。
【技术特征摘要】
1.一种硫吸附剂的再生方法，该方法包括：将含有镍组分的待生吸附剂送入再生器中与烧焦再生气体接触并进行烧焦再生，得到再生吸附剂；其特征在于，该方法还包括：将所得再生吸附剂送入再生器接收器中进行降温处理后，得到降温吸附剂，将部分所得降温吸附剂与所述待生吸附剂混合送入再生器中进行所述烧焦再生，将另一部分所得降温吸附剂用于送入反应器中进行吸附反应。2.根据权利要求1所述的再生方法，该方法还包括：向所述再生器中通入第一取热介质控制所述再生器的烧焦再生温度，所述第一取热介质包括选自氮气、二氧化碳、氦气和氩气中的至少一种惰性气体。3.根据权利要求1所述的再生方法，其中，通过向所述再生器接收器器中通入第二取热介质进行所述降温处理，所述第二取热介质包括选自氮气、二氧化碳、氦气和氩气中的至少一种惰性气体。4.根据权利要求1所述的再生方法，其中，控制所得降...
【专利技术属性】
技术研发人员：王文寿，毛安国，刘宪龙，张久顺，徐莉，刘玉良，
申请(专利权)人：中国石油化工股份有限公司，中国石油化工股份有限公司石油化工科学研究院，
类型：发明
国别省市：北京,11
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。