一种磁芯，其包括至少两个芯块及将所述至少两个芯块连接形成一个整体的粘结层。由于磁芯是由至少两个芯块分开制备再粘结成一个整体，进而可以满足较长尺寸、高密度、良好磁电性能的需要，比一体成型的磁芯密度更高，磁电性能更加优良，同时可以显著延长压机模具使用寿命，降低生产成本，适合在常规压力下批量规模化生产不同长度的磁芯。本发明专利技术还涉及一种具该磁芯的电感装置。

Magnetic core and inductance device with the magnetic core

A magnetic core includes at least two core blocks and a bonding layer which connects the at least two cores to form a whole. The core is composed of at least two core blocks separately prepared and bonded into a whole, and can meet the need of high density, long size, good magnetoelectric properties, higher density integrated, magnetoelectric properties more excellent, and can significantly prolong the service life of the press mold, reduce the production cost, suitable for the core production batch size in different length under normal pressure. The invention also relates to an inductance device with the magnetic core.

【技术实现步骤摘要】
磁芯及具该磁芯的电感装置
本专利技术涉及一种磁芯及具该磁芯的电感装置。
技术介绍
大电流用的电感磁芯往往采用金属磁粉芯。随着功率的增大，所要求的电感磁芯尺寸也不断增大。金属磁粉芯是由金属磁粉直接模压成型而来，由于没有烧结致密化工序，为了获得密度高、性能好的磁芯，需要高压制压力来保证高密度。磁粉芯尺寸越大，所需的压力也越高，否则就达不到所需要的磁性能。然而，提高压力易致使模具损坏或爆裂。
技术实现思路
有鉴于此，有必要提供一种避免上述问题的磁芯及具有该磁芯的电感装置。一种磁芯，所述磁芯包括至少两个芯块及将所述至少两个芯块连接形成一个整体的粘结层。进一步地，所述磁芯为圆柱体。进一步地，所述至少两个芯块为大小形状一致的扇形结构，所述芯块的弧度为2π/N，其中N为芯块的数量为大于等于2的整数。进一步地，每个芯块的边缘设有倒角。进一步地，所述芯块通过沿与所述磁芯的轴向方向相垂直的方向施加压力压制金属磁粉而成。进一步地，所述磁芯的轴向长度与横向宽度的比值大于1。进一步地，所述粘结层为胶水固化而成的胶层。进一步地，所述胶水为磁性胶水。进一步地，所述芯块的表面涂覆防锈液层。一种电感装置，其包括如上所述的本文档来自技高网...

【技术保护点】
一种磁芯，其特征在于：所述磁芯包括至少两个芯块及将所述至少两个芯块连接形成一个整体的粘结层。

【技术特征摘要】
1.一种磁芯，其特征在于：所述磁芯包括至少两个芯块及将所述至少两个芯块连接形成一个整体的粘结层。2.如权利要求1所述的磁芯，其特征在于：所述磁芯为圆柱体。3.如权利要求1所述的磁芯，其特征在于：所述至少两个芯块为大小形状一致的扇形结构，所述芯块的弧度为2π/N，其中N为芯块的数量且为大于等于2的整数。4.如权利要求1所述的磁芯，其特征在于：每个芯块的边缘设有倒角。5.如权利要求1所述的磁芯，其特征在于：所述芯块通过沿与所述磁...