本发明专利技术公开了一种钢塑复合瓦，其特征在于，包括从上到下依次排列且通过高温粘合为一体的三层，这三层分别是：耐候树脂构成的表层，镀锌钢板构成的骨架层，和热塑性树脂构成的底层。其中，耐候树脂层为PVC/ASA、PVC/PVDF或PVC/PMMA复合膜。本发明专利技术所制得的产品具有优异的防腐、耐老化性能，可有效延长产品使用寿命，拓宽产品的应用范围。

Steel plastic composite tile and its manufacturing method

The invention discloses a plastic composite tile, characterized by including are sequentially arranged from up to down and through high temperature adhesive layer three as a whole, the three layers are: weatherability resin composition of the surface layer of galvanized steel skeleton structure, and the bottom layer of a thermoplastic resin. Among them, the weather resistant resin layer is PVC/ASA, PVC/PVDF or PVC/PMMA composite film. The product prepared by the invention has excellent corrosion resistance and aging resistance, can effectively prolong the service life of the product, and broaden the application range of the product.

【技术实现步骤摘要】
钢塑复合瓦及其制造方法
技术介绍
本专利技术涉及一种屋面防水建材，具体涉及一种钢塑复合瓦。
技术介绍
目前，公知的彩钢涂板压型屋面瓦产品，是在镀锌钢板或类似材料表面喷涂有机涂料而成。由于喷涂镀锌钢板表面成膜厚度值小且不够致密，而造成在高温高湿尤其是在腐蚀性气体存在的环境下极易腐蚀生锈，而严重影响产品的使用寿命。也有使用PVC膜复合镀锌钢板产品，但因PVC膜受天候紫外光照射后容易老化，造成表面褪色、粉化、龟裂，而致使覆膜层下的钢板锈蚀。另外，现有钢塑复合工艺对覆膜层的粘结牢度影响较大，市售产品多存在覆膜层脱落的问题。
技术实现思路
本专利技术的目的是提供一种钢塑复合瓦，不仅寿命长，耐腐蚀，而且产品应用范围广。为实现上述目的，本专利技术公开了一种钢塑复合瓦，包括耐候树脂构成的表层、钢板构成的骨架层和热塑性树脂构成的底层，其中，所述耐候性树脂表层通过镀锌钢板涂胶层与钢板胶接，所述热塑性树脂底层为油漆通过喷涂工艺形成的均匀致密的涂层。进一步地，所述耐候树脂表层为复合膜结构，包括复合膜表层为ASA、PMMA、PVDF中的一种，底层为PVC。进一步地，上述两种钢塑复合瓦，所述耐候树脂表层的厚度为0.3-0.6本文档来自技高网...

【技术保护点】
一种钢塑复合瓦，包括耐候树脂构成的表层、钢板构成的骨架层和热塑性树脂构成的底层，其特征在于：所述耐候性树脂表层通过镀锌钢板涂胶层与钢板胶接，所述热塑性树脂底层为油漆通过喷涂工艺形成的均匀致密的涂层。

【技术特征摘要】
1.一种钢塑复合瓦，包括耐候树脂构成的表层、钢板构成的骨架层和热塑性树脂构成的底层，其特征在于：所述耐候性树脂表层通过镀锌钢板涂胶层与钢板胶接，所述热塑性树脂底层为油漆通过喷涂工艺形成的均匀致密的涂层。2.根据权利要求1所述的一种钢塑复合瓦，其特征在于：所述耐候树脂表层为复合膜结构，包括复合膜表层为ASA、PMMA、PVDF中的一种，底层为PVC。3.根据权利要求1或2所述的一种钢塑复合瓦，其特征在于：所述耐候树脂表层的厚度为0.3-0.6mm。4.根据权利要求2所述的一种钢塑复合瓦，其特征在于：所述的复合膜表层厚度为0.1-0.3mm，复合膜底层为0.2-0.5mm。5.根据权利要求1所述的一种钢塑复合瓦，其特征在于：所述的钢板骨架层为镀锌钢板。6...