The invention discloses a processing technology of high wear-resistant mold, which comprises the following steps: (100): the refined alloy cold die steel as mould material, and its refining, removal of impurities; (200) cold processing: the refined alloy cold die steel for cold working, through cold extrusion molding; (300) heat treatment: molding after salt bath heat treatment, in particular: salt bath quenching in 560 at a temperature of 590 DEG C, the quenching time is 30 40 minutes after quenching followed by air cooling; (400) surface treatment: to die after heat treatment for surface nitriding treatment. When the temperature is 720 DEG C 740, time of 5.5 6 hours. By adopting the method, the wear resistance of the die can be improved, the service life can be prolonged, and the long-term effect can be ensured.
【技术实现步骤摘要】
一种高耐磨模具的加工工艺
本专利技术涉及模具加工领域，特别是涉及一种高耐磨模具的加工工艺。
技术介绍
模具是在工业生产上用以注塑、吹塑、挤出、压铸或锻压成型、冶炼、冲压等方法得到所需产品的各种模子和工具。简而言之，模具是用来制作成型物品的工具，这种工具由各种零件构成，不同的模具由不同的零件构成。它主要通过所成型材料物理状态的改变来实现物品外形的加工。素有“工业之母”的称号。模具是在外力作用下使坯料成为有特定形状和尺寸的制件的工具。广泛用于冲裁、模锻、冷镦、挤压、粉末冶金件压制、压力铸造，以及工程塑料、橡胶、陶瓷等制品的压塑或注塑的成形加工中。模具具有特定的轮廓或内腔形状，应用具有刃口的轮廓形状可以使坯料按轮廓线形状发生分离(冲裁)。应用内腔形状可使坯料获得相应的立体形状。模具一般包括动模和定模（或凸模和凹模）两个部分，二者可分可合。分开时取出制件，合拢时使坯料注入模具型腔成形。模具是精密工具，形状复杂，承受坯料的胀力，对结构强度、刚度、表面硬度、表面粗糙度和加工精度都有较高要求。现有的模具由于要与工件产生无数次强烈的摩擦，同时使制件保持尺寸精度和表面粗糙度，需要具...
【技术保护点】
一种高耐磨模具的加工工艺，其特征在于，包括以下步骤：（100）精炼：选取合金冷作模具钢作为模具材料，并对其进行精炼，去除杂质；（200）冷加工：对精炼后的合金冷作模具钢进行冷加工，通过冷挤压成型；（300）热处理：对成型后的模具进行盐浴热处理，具体为：在560‑590℃温度下进行盐浴淬火，淬火时间为30‑40分钟，淬火结束后出炉空冷；（400）表面处理：对热处理后的模具进行表面氮化处理，处理时的温度为720‑740℃，时间为5.5‑6小时。
【技术特征摘要】
1.一种高耐磨模具的加工工艺，其特征在于，包括以下步骤：（100）精炼：选取合金冷作模具钢作为模具材料，并对其进行精炼，去除杂质；（200）冷加工：对精炼后的合金冷作模具钢进行冷加工，通过冷挤压成型；（300）热处理：对成型后的模具进行盐浴热处理，具体为：在560-590℃温度下进行盐浴淬火，淬火时间为30-40分钟...
【专利技术属性】
技术研发人员：贾宁霞，
申请(专利权)人：苏州市天星山精密模具有限公司，
类型：发明
国别省市：江苏,32