The invention relates to a waterproof concrete additive and a preparation method thereof, the additive by the raw materials with the following weight percentage of the composition of slag powder 25 40%; 25 40% silicon carbide powder; 5 15% 2 8%; sodium nitrite; ferric chloride 5 12%. The preparation method of the additive is simple and can be dispersed only by ball milling. Advantages: the pure inorganic additives by several specific combination (and does not contain any organic matter), by adjusting the ratio of scientific and reasonable, the components can produce synergistic effect, enhance the waterproof performance of the additive, and at the same time to ensure the strength of concrete, corrosion resistance and wear resistance improved using this additive to improve. The durability of concrete; the method is simple, the production efficiency of the high performance additives, additives and stability, easy storage.
【技术实现步骤摘要】
一种混凝土防水添加剂及其制备方法
本专利技术属于混凝土用添加剂领域，具体涉及一种混凝土防水添加剂及荣其制备方法。
技术介绍
混凝土建筑有时需要与水接触或长期浸泡在水中，需要混凝土有一定的防水抗渗性，比如公知、铁路隧道、地铁通道、深层矿井等均存在混凝土防水问题。现有的混凝土防水添加剂大都以硫酸盐或铝酸盐等材料为主体，同时配合使用一些有机物(胺类、有机硅、脂肪酸、聚丙烯酸纤维、聚乙烯醇等)，其虽对混凝土的抗渗防水能力有一定提升，但由于硫酸盐或铝酸盐本身为对混凝土性能不利的物质，导质混凝土的强度、耐蚀、耐磨等下降，有机物与混凝土浆料的相容性差，生产时通常对搅拌混合的要求较高，导致生产效率和生产成本增加。
技术实现思路
本专利技术提供一种混凝土防水添加剂及其制备方法，旨在一定程度上克服现有技术中已有混凝土防水添加剂的不足，确保防水添加剂既能提升混凝土的防水能力，又能保证较好强度、耐蚀和耐磨等性能。本专利技术解决上述技术问题的技术方案如下：一种混凝土防水添加剂，其由以下质量百分数的各原料组成：矿渣粉25-40％；硅粉25-40％；碳化硅粉5-15％；亚硝酸钠2-8％；氯化铁5-...
【技术保护点】
一种混凝土防水添加剂，其特征在于，由以下质量百分数的各原料组成：矿渣粉25‑40％；硅粉25‑40％；碳化硅粉5‑15％；亚硝酸钠2‑8％；氯化铁5‑12％。
【技术特征摘要】
1.一种混凝土防水添加剂，其特征在于，由以下质量百分数的各原料组成：矿渣粉25-40％；硅粉25-40％；碳化硅粉5-15％；亚硝酸钠2-8％；氯化铁5-12％。2.根据权利要求1所述的一种混凝土防水添加剂，其特征在于，由以下重量百数的各原料组成：矿渣粉30-35％；硅粉35-40％；碳化硅粉8-12％；亚硝酸钠4-8％；氯化铁8-10％。3.根据权利要求1所述的一种混凝土防水添加剂，其特征在于，所述矿渣粉为超细矿渣粉，其比表面积为4500-7500cm2/g。4.根据权利要求1所述的一种混凝土防水添加剂，其特征在于，所述硅粉的粒径为600-2500目。5.根据权利要...