The invention relates to the field of building materials, in particular to the preparation method of weak base liquid accelerator. The preparation process includes sodium hydroxide, potassium hydroxide, aluminum hydroxide were added into water, at a temperature of 95~120 DEG C, the reaction of 2 ~ 3H by Aluminate mother liquor; sodium fluoride will be first dissolved in water at a certain temperature and then adding the silicate aqueous solution, prepared modifier; finally the modifier adding sulphoalminate composite liquor, after full reaction, make the new type of liquid low alkali accelerator of the invention. The accelerator has the characteristics of short setting time, low alkali content and good adaptability of cement.
【技术实现步骤摘要】
一种弱碱液态速凝剂的制作方法
本专利技术涉及建筑材料领域，具体涉及一种弱碱液态速凝剂的制作方法。
技术介绍
速凝剂是能够使混凝土或砂浆迅速凝结硬化的外加剂，主要用于喷射混凝土、砂浆机堵漏抢险工程。喷射混凝土用液体速凝剂，改善了粉剂混合不均匀、粉尘大、施工环境差的缺点，加快了混凝土拌合物的凝结，提高了早期强度，这样可以增加喷层厚度并缩短喷射下一下的时间，大大扩展了其使用范围。液体速凝剂主要包括无碱液体速凝剂和铝酸盐类液体速凝剂，其作用效果与水泥中的矿物组分差异明显。无碱液体速凝剂的主要组分为硫铝酸盐，由于其价格高、掺量大(4～10％)，前期强度较低，从而影响了材料的广泛使用，如CN00816806.7将硫酸铝和无定形氢氧化铝溶于含有胺的水中，添加一种非碱性盐的稳定剂合成的无碱液体速凝剂对波兰特水泥的掺量为7％；CN200910028321.1以硫酸铝和金属氟化钠为主要成分，添加部分胺类物质和调节剂，制备出的无碱速凝剂，存在成本高、掺量大和长时间存储出现沉淀和絮凝现象；专利CN200580046556.3是以含氟化钠的铝络合物水溶液为主要成分的液体促凝剂，虽其低温稳定...
【技术保护点】
一种弱碱液态速凝剂的制作方法，其特征在于：包括以下步骤：（1）铝酸盐复合母液制备：将氢氧化钠、氢氧化钾、氢氧化铝加入到水中，然后加热到95～120℃，反应2～3h的得到铝酸盐母液；所述氢氧化铝为20～40%、氢氧化钠为15～25%、氢氧化钾为15～25%、水为20～40%，且氢氧化钠和氢氧化钾的质量比为1：（1～1.5）；(2)改性剂的制备：将氟化钠先溶解于水中，然后加热到30～60℃，再将硅酸盐加入到氟化钠水溶液中，形成透明的溶液,所述的氟化钠质量为3～10%、硅酸盐为5～20%、水为50～90%；（3）新型低碱液体速凝剂的制备将步骤（2）制备的改性剂滴加到步骤（1）制备...
【技术特征摘要】
1.一种弱碱液态速凝剂的制作方法，其特征在于：包括以下步骤：（1）铝酸盐复合母液制备：将氢氧化钠、氢氧化钾、氢氧化铝加入到水中，然后加热到95～120℃，反应2～3h的得到铝酸盐母液；所述氢氧化铝为20～40%、氢氧化钠为15～25%、氢氧化钾为15～25%、水为20～40%，且氢氧化钠和氢氧化钾的质量比为1：（1～1.5）；(2)改性剂的制备：将氟化钠先溶解于水中，然后加热到30～6...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。