The invention discloses a cement foaming agent, relates to the field of building material, the cement foaming agent formula by telomerization of perfluorinated octyl alcohol, butane, pentane, two methyl two benzoyl peroxide, two phenyl phosphine as raw material, which belongs to the physical foaming agent, especially creatively added two benzene peroxide and two formyl phenyl phosphine, with high surface activity, can effectively reduce the surface tension of the liquid, and the liquid surface electric double layer arrangement and surrounded by air bubble formation, and then by a single bubble bubble. The cement foaming agent has a strong dispersing effect on cement particles, enlarges the contact area of cement and water, promotes hydration reaction, reduces water consumption, and improves the strength, compactness and impermeability of cement.
【技术实现步骤摘要】
水泥发泡剂配方
本专利技术涉及建筑材料领域，具体来说涉及一种水泥发泡剂配方。
技术介绍
发泡水泥是通过发泡机的发泡系统将发泡剂用机械方式充分发泡，并将泡沫与水泥浆均匀混合，然后经过发泡机的泵送系统进行现浇施工或模具成型，经自然养护所形成的一种含有大量封闭气孔的新型轻质保温材料。现有的水泥发泡剂使用的原料比较传统，导致发泡效果不佳，致使发泡水泥的保暖性不能进一步提高。
技术实现思路
本专利技术所要解决的问题是提供一种水泥发泡剂配方，具有良好的发泡效果，提高了发泡水泥板材的使用性能。为了实现上述目的，本专利技术采取的技术方案为：一种水泥发泡剂配方，其特征在于，该水泥发泡剂配方包括如下质量份数的组分：32～45份调聚全氟辛基乙醇、26～33份正丁烷、12～19份二甲基戊烷、14～22份过氧化二苯甲酰、5～8份二苯基膦。有益效果：该水泥发泡剂配方采用调聚全氟辛基乙醇、正丁烷、二甲基戊烷、过氧化二苯甲酰、二苯基膦为原料，属于物理发泡剂，尤其是创造性地添加了过氧化二苯甲酰和二苯基膦，具有较高的表面活性，能有效降低液体的表面张力，并在液膜表面双电子层排列而包围空气，形成气泡，再由单个气泡组成泡沫。该水泥发泡剂对水泥颗粒有强烈的分散作用，扩大了水泥和水的接触面积，促进水化反应，减少用水量，提高水泥的强度、密实性和抗渗性。具体实施方式实施例1：该水泥发泡剂配方包括如下质量份数的组分：32份调聚全氟辛基乙醇、33份正丁烷、12份二甲基戊烷、14份过氧化二苯甲酰、8份二苯基膦。实施例2：该水泥发泡剂配方包括如下质量份数的组分：39份调聚全氟辛基乙醇、28份正丁烷、15份二甲基戊烷、...
【技术保护点】
一种水泥发泡剂配方，其特征在于，该水泥发泡剂配方包括如下质量份数的组分：32～45份调聚全氟辛基乙醇、26～33份正丁烷、12～19份二甲基戊烷、14～22份过氧化二苯甲酰、5～8份二苯基膦。
【技术特征摘要】
1.一种水泥发泡剂配方，其特征在于，该水泥发泡剂配方包括如下质量份数的组分：32～45份调聚全氟辛...
【专利技术属性】
技术研发人员：黄文华，任娟，宋婉恬，
申请(专利权)人：陕西理工学院，
类型：发明
国别省市：陕西,61