This case discloses a rare earth magnesium nodulizing agent comprises the following parts by weight of material: 60 to 62 parts by weight of a rubidium oxide silicon, 3 to 5 parts by weight of calcium, 6 to 8 parts by weight of magnesium, 0.3 to 0.5 parts by weight of sulfur, 25 to 27 parts by weight of iron, 1 ~ 3 the weight of La, 0.2 to 0.4 parts by weight of Gd, 0.5 to 1.5 parts by weight of barium, 0.05 to 0.1 parts by weight of molybdenum, 0.05 to 0.1 parts by weight of 0.05 to 0.1 parts by weight of cerium, yttrium and 0.005 to 0.01 parts by weight. In the case of the composite rare earth magnesium ball improved optimization formulation, the introduction of a variety of elements has a synergistic effect, improve the spheroidization agent on the graphite rate, while reducing the depth of white spheroidizer on cast iron.
【技术实现步骤摘要】
一种稀土镁球化剂
本专利技术涉及一种球化剂,尤其涉及一种处理球墨铸铁稀土镁球化剂。
技术介绍
在铸铁时,会含有2~4%的碳,这种碳会与铁紧密结合,而碳在凝固的铸铁中的形态对于铸铁件的性能是非常重要的。若这种碳呈碳化铁的形态,则该铸铁被称为白口铁,它硬而脆,实用性很差。若碳呈石墨态,该铸铁软,易于加工,其被称为灰铸铁,实用性强。石墨态又可分为片状、致密状和球状,其中球状形态能够展现出最高的强度及最可延展形态的铸铁。在铸铁凝固过程中,使石墨形成球状的添加剂称为球化剂。通常,以石墨球化率和白口深度来衡量球化剂的优劣。虽然在现有技术已有一些比较成熟的球化剂,但从节约成本、缩短工艺、减少稀土使用量、减少污染、降低球化剂添加量、降低白口倾向和增大球化率等角度去看,球化剂依然有很大的改进空间。
技术实现思路
针对上述技术缺陷,本专利技术的目的在于提供一种具有更低白口倾向和更高球化率的复合型稀土镁球化剂。本专利技术的技术方案概述如下:一种稀土镁球化剂,包括以下重量份的材料:优选的是,所述的稀土镁球化剂,还包括0.5~1.5重量份的钡和0.05~0.1重量份的钼。优选的是,所述的稀土镁球化剂,还包括0.05~0.1重量份的铈。优选的是,所述的稀土镁球化剂,还包括0.05~0.1重量份的钇。优选的是,所述的稀土镁球化剂,还包括0.005~0.01重量份的氧化铷。本专利技术的有益效果是:通过对复合型稀土镁球化剂配方的改进优化,引入了多种具有协效作用的元素,提高了球化剂对石墨的球化率,同时降低了球化剂对铸铁的白口深度。具体实施方式下面结合实施例对本专利技术做进一步的详细说明,以令本领 ...
【技术保护点】
一种稀土镁球化剂,包括以下重量份的材料:
【技术特征摘要】
1.一种稀土镁球化剂,包括以下重量份的材料:2.根据权利要求1所述的稀土镁球化剂,其特征在于,还包括0.5~1.5重量份的钡和0.05~0.1重量份的钼。3.根据权利要求1所述的稀土镁球化剂,其特征在于,还...