The invention discloses a graphene conductive composite material and its preparation method, graphene conductive composite material, which is composed of graphene nanosheets, carbon nanotubes, carbon black and conductive polymer matrix composition, weight of each component are as follows: graphene nanosheets from 0.01 to 10, the carbon nano tubes from 1 to 10, conductive carbon black 5 - 20, 10 to 100 portions of the polymer matrix. The invention of graphene nanosheets first supported on carbon nanotubes, and then with the load in the polymer matrix, so that the conductive composite material of the invention of the guide has been improved, and the invention provides a preparation method for the operation of graphene composite filler is simple, uniform dispersion, preparation quality the conductive composite material, conductive performance.
【技术实现步骤摘要】
一种石墨烯导电复合材料及其制备方法
本专利技术涉及复合材料
，特别涉及一种石墨烯导电复合材料及其制备方法。
技术介绍
石墨烯是一种有sp2杂化的碳原子紧密堆积而成的二维蜂窝状晶格结构的碳质新材料，厚度为一个或多个原子层。石墨烯表现出优异的电子传输能力，室温下其电子迁移率高达15000cm2/V·S。制备高性能石墨烯/聚合物导电复合材料的关键在于获得层数单一的石墨烯及石墨烯在聚合物中的均匀分散。到目前为止，石墨烯可通过一下四种方法得到：化学汽相沉积法、外延生长法、机械剥离法及氧化还原法，只有氧化还原法使得大量石墨烯应用于复合材料。石墨烯/聚合物复合材料可以实现材料的优势互补与加强，石墨烯可以极大地提高聚合物材料的机械性能，这是由于石墨烯具有高的比表面积，强的纳米材料—基体界面作用和sp2杂化的优良机械性能。石墨烯/聚合物复合材料具有良好的导电性，可以广泛应用于超级电容器、汽车防静电挡泥板、门把手、镜盒及周转箱等。目前石墨烯/聚合物复合材料的制备方法可采用熔融、溶液及原位还原法，但是只有熔融共混的方法可以实现工业化生产，可是随之而来的问题是石墨烯在自团聚问题，这...
【技术保护点】
一种石墨烯导电复合材料，其特征在于，其由石墨烯纳米片、碳纳米管、导电炭黑以及聚合物基体组成，各组分的重量份如下：石墨烯纳米片0.01～10份、碳纳米管1～10份、导电炭黑5～20份、聚合物基体10～100份。
【技术特征摘要】
1.一种石墨烯导电复合材料，其特征在于，其由石墨烯纳米片、碳纳米管、导电炭黑以及聚合物基体组成，各组分的重量份如下：石墨烯纳米片0.01～10份、碳纳米管1～10份、导电炭黑5～20份、聚合物基体10～100份。2.根据权利要求1所述的石墨烯导电复合材料，其特征在于，所述石墨烯纳米片表面负载有两亲性大环化合物。3.根据权利要求1所述的石墨烯导电复合材料，其特征在于，所述聚合物基体为水溶性聚氨酯、聚乙烯醇、水溶性环氧树脂和水溶性丙烯酸树脂中的一种...
【专利技术属性】
技术研发人员：汪泽维，黄浩，郭伟，
申请(专利权)人：合肥泓定科技有限公司，
类型：发明
国别省市：安徽,34