一种碳化氮纳米片及其制备方法和应用技术
A carbon nitride nano film and preparation method and application thereof
The invention belongs to the technical field of nano materials synthesis, polymerization step synthesis Shi Moxiang carbonization nitrogen use simple and direct rapid heat (g C3N4) nano film photocatalyst for photocatalytic decomposition of water to hydrogen. The melamine in circular crucible, and then put the flat on the top of the melamine foam nickel, then cover the crucible lid, and flat in the muffle furnace, the initial temperature of 50 DEG to 2.3 DEG /min, the heating rate of the muffle furnace is heated to 500 DEG C 550 DEG C, and the reaction temperature 4h, preferably 550 DEG C, cooled to room temperature after get carbon nitride nanosheets of nickel foam and the corresponding lower upper black.
【技术实现步骤摘要】
一种碳化氮纳米片及其制备方法和应用
本专利技术属于纳米材料合成
，利用简单直接快速的热聚合法一步合成类石墨相碳化氮(g-C3N4)纳米片光催化剂，可用于可见光下光催化分解水产氢气。
技术介绍
近年来，环境污染和能源紧缺等一系列全球性问题对人类的发展产生了越来越严重地影响，政府和科学家们正在寻求一种绿色可持续的有效替代方法来解决上述问题，在过去的近四十年里，光催化分解水制氢因具有经济、环保、可再生、安全等优点，已成为解决问题的热门研究课题，光催化技术利用绿色和无污染的太阳光既可以实现分解水制氢气，还可以分解污染物达到改善环境的目的。众所周知，纳米材料因具有颗粒尺寸小、比表面积大、表面能高、表面原子所占比例大等特点，以及其特有的三大效应(表面效应、小尺寸效应和宏观量子隧道效应)，被称为21世纪“最有前途的材料”，因此，开发可实际应用的纳米级的半导体光催化剂是当前光催化研究领域的重要课题。类石墨相非金属半导体碳化氮(g-C3N4)作为一种有机半导体由于具有良好的物理和化学稳定性、可见光响应、非金属的组成、低廉的成本、安全无毒等特点，被公认为优秀的光催化剂，在光催化...
【技术保护点】
一种碳化氮纳米片，其特征在于，采用如下步骤制备：称取三聚氰胺置于圆形坩埚中，然后将处理好的泡沫镍平放于三聚氰胺之上，接着盖上坩埚盖，并平置于马弗炉中，初始温度为50℃，以2.3℃/min的升温速率将马弗炉升温至500℃‑550℃，并在该温度下反应4h，自然冷却至室温后，得到上层黑色的泡沫镍和下层相应的碳化氮纳米片。
【技术特征摘要】
1.一种碳化氮纳米片，其特征在于，采用如下步骤制备：称取三聚氰胺置于圆形坩埚中，然后将处理好的泡沫镍平放于三聚氰胺之上，接着盖上坩埚盖，并平置于马弗炉中，初始温度为50℃，以2.3℃/min的升温速率将马弗炉升温至500℃-550℃，并在该温度下反应4h，自然冷却至室温后，得到上层黑色的泡沫镍和下层相应的碳化氮纳米片。2.如权利要求1所述的一种碳化氮纳米片，其特征在于，升温至550℃。3.如权利要求1所述的一种碳化氮纳米片，其特征在于，所述泡沫镍的处理方法为：将泡沫镍洗涤后，干燥待用。4.如权...
【专利技术属性】
技术研发人员：施伟东，方振远，洪远志，殷秉歆，罗必富，
申请(专利权)人：江苏大学，
类型：发明
国别省市：江苏,32