The invention discloses a high temperature resistant ceramic fiber composite brake pad and preparation method thereof, including phenolic resin, rubber, Ding Jing clay, ceramic fiber, graphite fiber, glass fiber, steel fiber, gelatin, rosin, zinc stearate, styrene acrylonitrile copolymer acrylic rubber, PMMA, boric acid and mixed nano elemental tungsten mixing, mixing; the material obtained in mold, compression molding, and then forming material for curing. The invention is mainly by adding clay, ceramic fiber, graphite fiber, glass fiber, steel fiber, gelatin, rosin, styrene acrylonitrile copolymer, acrylic rubber PMMA, boric acid, nano elemental tungsten first based on the original material, so as to improve the wear resistance of the ceramic brick and high temperature performance.
【技术实现步骤摘要】
高温耐磨陶瓷复合纤维刹车片及其制备方法
本专利技术涉及机械配件
，尤其是一种陶瓷复合纤维刹车片。
技术介绍
陶瓷复合纤维刹车片是刹车片的一种，目前主要是由陶瓷纤维、不含铁的填料物质、胶粘剂和少量金属等原料制成。其相对于传统的刹车片，陶瓷复合纤维刹车片更清洁安静，并且在提供卓越刹车性能的同时，不磨耗对偶件。然而，尽管陶瓷复合纤维刹车片具备上述功能，但是其也存在着一些缺点，例如，其耐磨性能和耐高温较差，使用时损耗大，使用寿命短。
技术实现思路
本专利技术提供一种高温耐磨陶瓷复合纤维刹车片及其制备方法，它可以解决现有陶瓷复合纤维刹车片存在耐磨性能和耐高温较差的问题。为了解决上述技术问题，本专利技术所采用的技术方案是：它采用以下重量份数的原料：酚醛树脂45份～50份、丁腈橡胶15份～20份、粘土15份～20份、陶瓷纤维15份～20份、石墨纤维10份～15份、玻璃纤维1份～5份、钢纤维5份～10份、明胶5份～10份、松香5份～10份、硬脂酸锌5份～10份、苯乙烯-丙烯腈-压克力橡胶共聚物5份～10份、聚甲基丙烯酸甲酯5份～10份、硼酸5份～10份以及纳米单质钨1份～5份；...
【技术保护点】
一种高温耐磨陶瓷复合纤维刹车片，其特征在于由以下重量份数的原料制成：酚醛树脂45份～50份、丁腈橡胶15份～20份、粘土15份～20份、陶瓷纤维15份～20份、石墨纤维10份～15份、玻璃纤维1份～5份、钢纤维5份～10份、明胶5份～10份、松香5份～10份、硬脂酸锌5份～10份、苯乙烯‑丙烯腈‑压克力橡胶共聚物5份～10份、聚甲基丙烯酸甲酯5份～10份、硼酸5份～10份以及纳米单质钨1份～5份。
【技术特征摘要】
1.一种高温耐磨陶瓷复合纤维刹车片，其特征在于由以下重量份数的原料制成：酚醛树脂45份～50份、丁腈橡胶15份～20份、粘土15份～20份、陶瓷纤维15份～20份、石墨纤维10份～15份、玻璃纤维1份～5份、钢纤维5份～10份、明胶5份～10份、松香5份～10份、硬脂酸锌5份～10份、苯乙烯-丙烯腈-压克力橡胶共聚物5份～10份、聚甲基丙烯酸甲酯5份～10份、硼酸5份～10份以及纳米单质钨1份～5份。2.一种高温耐磨陶瓷复合纤维刹车片的制备方法，其特征在于：采用以下重量份数的原料：酚醛树脂45份～50份、丁腈橡胶15份～20份、粘土15份～20份、陶瓷纤维15份～20...
【专利技术属性】
技术研发人员：何兴保，何圣贤，
申请(专利权)人：柳州金特新型耐磨材料股份有限公司，
类型：发明
国别省市：广西,45