用于电化学还原二氧化碳的催化剂及其制备方法技术
Catalyst for electrochemical reduction of carbon dioxide and preparation method thereof
To provide a method for the electrochemical reduction of carbon dioxide catalyst, the catalyst is a carbon supported nano AgxZnyOz or AgxZny alloy, 0< x< 0< 1, y< 1, x+y = 1, z = 2x+y. A method for the preparation of the catalyst is also provided. The particle size of the active component of the two catalysts reaches the nanometer level, which ensures that the catalyst has many active sites and has a large current density. The catalyst has good electrocatalytic activity for CO2 reduction, not only the electrolysis voltage is low, but also the CO2 conversion efficiency is high. The two methods of catalyst preparation have good process amplification ability, their core steps are complex decomposition precipitation, or dipping roasting process, they are simple and easy to control.
【技术实现步骤摘要】
用于电化学还原二氧化碳的催化剂及其制备方法
本专利技术涉及一种电化学还原领域，尤其涉及一种用于电化学还原二氧化碳的催化剂及其制备方法。
技术介绍
化石燃料的广泛使用不仅消耗了大量的能源，带来了能源问题，而且产生的大量CO2若直接排放，则会带来严重的环境问题。另一方面CO2也是一种丰富的碳源，若将CO2转变成有用的物质，则不失为一种解决相关能源问题和环境问题的方案。CO2是一种稳定的化合物，通过电化学还原方法实现CO2的转化是一种有效的途径，但其转化效果在较大程度上取决于CO2电还原催化剂的性能及其制备方法。研究较多的CO2电还原催化剂包括Cu、Ag、Au、In、Sn、Pb和Zn等。中国专利201110078394.9以In、Sn、Pb或Zn等金属片作为阴极催化剂，中国专利201210408760.7以Pb片作为阴极催化剂。直接采用大面积金属作为电极从电还原催化剂制备来讲固然简单，但催化剂活性位点少、CO2电还原活化能高，导致CO2电还原活性低下，析氢副反应偏重发生，因而电解池电压高、CO2转化电流效率(二氧化碳电还原电流在总电流中的比例)低。中国专利2011800...
【技术保护点】
一种用于电化学还原二氧化碳的催化剂，其特征在于，所述催化剂是碳负载纳米AgxZnyOz，其中0<x<1，0<y<1，x+y＝1，z≤2x+y。
【技术特征摘要】
1.一种用于电化学还原二氧化碳的催化剂，其特征在于，所述催化剂是碳负载纳米AgxZnyOz，其中0<x<1，0<y<1，x+y＝1，z≤2x+y。2.一种用于电化学还原二氧化碳的催化剂，其特征在于，所述催化剂为纳米AgxZny合金，其中0<x<1，0<y<1，x+y＝1。3.根据权利要求1或2所述的催化剂，其特征在于，0<x≤0.5。4.根据权利要求1所述的催化剂，其特征在于，所述纳米AgxZnyOz的晶粒尺寸为20-30nm。5.根据权利要求2所述的催化剂，其特征在于，所述纳米AgxZny合金中形成有锌银固溶体。6.一种制备根据权利要求1所述的用于电化学还原二氧化碳的催化剂的方法，其特征在于，包括如下步骤：S1：按摩尔比称取可溶性锌源化合物和银源化合物，将所述锌源化合物和银源化合物溶解在...
【专利技术属性】
技术研发人员：赵鹏鹃，张红飞，康鹏，
申请(专利权)人：碳能科技北京有限公司，
类型：发明
国别省市：北京,11