A wear resistant material and iron smelting method, consisting of the following materials: iron weight: 75 85 carbon: 8 10, copper 16: 12: 3, 8, silicon manganese chromium 6: 4: 5, 8. Method for smelting iron wear-resistant materials, according to the following process: (1) filled with slag in the bottom; (2) to join the scrap and start heating to dissolve iron; (3) adding phosphorus desulfurization agent, to add a certain amount of residual scrap, scrap, to stop; (4) to join to a certain amount of residual ferrochrome, stop adding ferrochrome, the remaining scrap addition, then add all the iron; the iron casting process, through composition design and reasonable steps, the raw material and the mold can be reused, high production efficiency, can realize the recycling of scrap iron and scrap castings save, casting materials, reduce production cost, improve the appearance and quality of castings.
【技术实现步骤摘要】
一种耐磨铁件材料及冶炼方法
本专利技术涉及铸造
，具体为一种耐磨铁件材料及冶炼方法。
技术介绍
铸铁属于二次加工，可制成复杂的零件，具有优良的铸造性、切削加工性、耐磨性和消震性，其是冶金厂的重要初级产品，大部分用于炼钢，另一部分供给及其制造厂生产铸铁件，作为二次重熔的主要炉料，现代机器设备中60～70％的重量为铸铁件。铸铁的最终性能受很多因素的影响，比如：冶炼原料的成分和配比、冶炼时温度的控制、冶炼时原料加入的顺序、孕育剂的使用、铁水浇筑时的温度时间、铸件的后期热处理等，每个因素均需要很注意才能保证铸铁铸件的机械性。
技术实现思路
本专利技术要解决的技术问题是提供一种耐磨铁件材料及冶炼方法，以解决上述
技术介绍
中提出的问题。为实现上述技术目的，达到上述技术效果，本专利技术通过以下技术方案实现：一种耐磨铁件材料，由下列原料的重量份组成：铁：75-85，碳：8-10，铜：12-16，硅：3-8，锰：4-6，铬：5-8。一种耐磨铁件材料的冶炼方法，按照如下冶炼过程：(1)在炉底放满造渣剂；(2)继续加入废铁并开始加热至废铁溶解；(3)加入脱硫磷剂，继续加入废铁，剩余一定...
【技术保护点】
一种耐磨铁件材料，其特征在于，由下列原料的重量份组成：铁：75‑85，碳：8‑10，铜：12‑16，硅：3‑8，锰：4‑6，铬：5‑8。
【技术特征摘要】
1.一种耐磨铁件材料，其特征在于，由下列原料的重量份组成：铁：75-85，碳：8-10，铜：12-16，硅：3-8，锰：4-6，铬：5-8。2.一种耐磨铁件材料的冶炼方法，其特征在于：按照如下冶炼过程：(1)在炉底放满造渣剂；(2)继续加入废铁并开始加热至废铁溶解；(3)加入脱硫磷剂，继续加入废铁，剩余一定量时，停止加入废铁；(4)开始加入铬铁至剩余一定...
【专利技术属性】
技术研发人员：宋有根，
申请(专利权)人：池州市超杰机电设备有限公司，
类型：发明
国别省市：安徽,34