The present invention discloses a five oxidation two vanadium bonded silicon carbide refractory material, comprising 80~120 high-purity silicon carbide powders, 0.2 to 2 parts, five oxidized two vanadium powder and 1~5 aluminium silicon alloy powder. The invention also discloses a preparation method of the five oxidation two vanadium bonded silicon carbide refractory material. Five of two vanadium as pore filler and sintering promoting agent, five of two vanadium will make pores between the silicon carbide particles during sintering, and during sintering also can promote sintering effect, improve the Sintering Densification, improve the strength of materials. Al Si alloy powder is an antioxidant. Al Si alloy will preferentially react with the silicon carbide in the process of combustion, and form a dense structure at the same time, which will improve the oxidation resistance and mechanical properties.
【技术实现步骤摘要】
一种五氧化二钒结合碳化硅耐火材料
本专利技术涉及一种耐火材料，特别是一种五氧化二钒结合碳化硅耐火材料及其制备方法。
技术介绍
干熄焦是干法熄灭炽热焦炭的简称。干熄焦装置装置斜道区耐火材料使用环境恶劣，易损坏，寿命短。传统的斜道区使用的耐火材料是莫来石-碳化硅材料，其具有良好的抗氧化性、较好的热震稳定性、耐磨损和抗侵蚀性能；而新兴的氮化硅结合碳化硅材料因具有耐高温、高温强度大、热抗震等优异性能，而且还会发生氮化不透的问题。
技术实现思路
专利技术目的：本专利技术的目的在于解决现有的氮化硅结合碳化硅材料斜道区耐火材料易损坏，寿命短的问题。技术方案：本专利技术采用以下技术方案：一种五氧化二钒结合碳化硅耐火材料，按照重量份数包括80～120份高纯碳化硅粉、0.2～2份五氧化二钒粉和1～5份铝硅合金粉。作为优化，还包括4～10份结合剂，所述结合剂包括糊精和硅溶胶。作为优化，所述高纯碳化硅的碳化硅含量超过98％。作为优化，所述铝硅合金粉的粒径不超过2微米。作为优化，所述五氧化二钒粉的粒径不超过5微米。一种五氧化二钒结合碳化硅耐火材料的制备方法，包括以下步骤：1)将五氧化二钒粉和原...
【技术保护点】
一种五氧化二钒结合碳化硅耐火材料，其特征在于：按照重量份数包括80～120份高纯碳化硅粉、0.2～2份五氧化二钒粉和1～5份铝硅合金粉。
【技术特征摘要】
1.一种五氧化二钒结合碳化硅耐火材料，其特征在于：按照重量份数包括80～120份高纯碳化硅粉、0.2～2份五氧化二钒粉和1～5份铝硅合金粉。2.根据权利要求1所述的五氧化二钒结合碳化硅耐火材料，其特征在于：还包括4～10份结合剂，所述结合剂包括糊精和硅溶胶。3.根据权利要求1所述的五氧化二钒结合碳化硅耐火材料，其特征在于：所述高纯碳化硅的碳化硅含量超过98％。4.根据权利要求1所述的五氧化二钒结合碳化硅耐火材料，其特征在于：所述铝硅合金粉的粒径不超过2微米。5.根据权利要求1所述的五氧化二钒结合碳化硅耐火材料，其特征在于：所述五...
【专利技术属性】
技术研发人员：董良军，程平平，李亚伟，桑绍柏，
申请(专利权)人：宜兴市丁山耐火器材有限公司，
类型：发明
国别省市：江苏,32