The invention provides a PC windshield plate injection molding method, which comprises the following steps: (1) PC in the 110 120 deg.c for 8 12 hours standby; (2) the PC will join the injection molding machine, heating to soften, then self-healing microcapsules with silane coupling agent, adding injection molding machine, mixing, injection molding, namely PC windshield plate. The invention uses self-healing microcapsules modified on the PC windshield plate, making the glass surface received minor trauma can automatically recover, prevent scratches on the surface of light transmission and visual effects, improved safety. The stability of the glass plate is improved by injection molding and tempering.
【技术实现步骤摘要】
一种PC挡风玻璃板注塑方法
本专利技术涉及注塑
，尤其涉及一种PC挡风玻璃板注塑方法。
技术介绍
挡风玻璃板是用于摩托车上的一个配件，其传统材料主要为聚甲基丙烯酸甲酯(PMMA)，制备方法则是采用热成型制备PMMA板材，再将其冲裁成需要的形状，但这样的加工方式存在容易划伤板材表面、生产工序多、效益低、板材浪费较大等缺陷。而若将材料换成聚碳酸酯(PC)，就可以通过注射成型的方法来较好地解决热成型加工的缺陷，并大幅提升生产效率和制品表面质量。挡风玻璃板属于外观件，表面要求高，不能有银丝、缩痕、气斑、雾斑和变形等缺陷。
技术实现思路
本专利技术目的就是为了弥补已有技术的缺陷，提供一种PC挡风玻璃板注塑方法。本专利技术是通过以下技术方案实现的：一种PC挡风玻璃板注塑方法，步骤为：(1)将PC在110-120℃下干燥8-12小时，备用；(2)将PC加入注塑机中，加热至软化，再将自愈合微胶囊用硅烷偶联剂处理，加入注塑机中，混合均匀，注塑成型，即得PC挡风玻璃板。硅烷偶联剂处理处理方法是将硅烷偶联剂溶于水中，制成4-5wt%的溶液，加入自愈合微胶囊，搅拌均匀，过滤干燥，即得。...
【技术保护点】
一种PC挡风玻璃板注塑方法，其特征在于，步骤为： (1)将PC在110‑120℃下干燥8‑12小时，备用；(2)将PC加入注塑机中，加热至软化，再将自愈合微胶囊用硅烷偶联剂处理，加入注塑机中，混合均匀，注塑成型，即得PC挡风玻璃板。
【技术特征摘要】
1.一种PC挡风玻璃板注塑方法，其特征在于，步骤为：(1)将PC在110-120℃下干燥8-12小时，备用；(2)将PC加入注塑机中，加热至软化，再将自愈合微胶囊用硅烷偶联剂处理，加入注塑机中，混合均匀，注塑成型，即得PC挡风玻璃板。2.如权利要求1所述PC挡风玻璃板注塑方法，其特征在于，硅烷偶联剂处理处理方法是将硅烷偶联剂溶于水中，制成4-5wt%的溶液，加入自愈合微胶囊，搅拌均匀，过滤干燥，即得。3.如权利要求1所述PC挡风玻璃板注塑方法，其特征在于，注塑温度为喷嘴290-295℃、注塑第1段305-310℃、注塑第2段310-315℃、注塑第3段295-298℃、注塑第4段280-284℃、热流道温度均为283-285℃。4.如权利要求1所述PC挡风玻璃板注塑方法，其特征在于，注塑的压力为：第1段9-9.5MPa、注塑第2段11-12MPa、注塑第3段8.5-8.8MPa、注塑第4段7-7.5MPa。5.如权利要求1所述PC挡风玻璃板注塑方法，其特征在于，注塑后取出成玻璃板，再进行回火处理，温度为120-125℃，时间为10-15分钟。6.如权利要求1所述PC挡风玻璃板注塑方法，其特...
【专利技术属性】
技术研发人员：查国东，储振亚，储亮，李云雷，查卫东，
申请(专利权)人：岳西县同兴尼龙橡胶制品有限公司，