The invention discloses a preparation method of a refractory castable, belonging to the technical field of unshaped refractory material preparation. The invention uses sodium bicarbonate as the first puffing aid, under high temperature and high pressure, so the rice husk pyrolysis and loose structure, followed by low temperature carbonization and high temperature sintering, the formation of silicon carbide whiskers with graphite as raw material, after freeze pulverizing and alumina mixing granulation, the zirconium boride and three methyl epichlorohydrin mixing and drying, to produce silicon carbide by three methyl epichlorohydrin under high temperature decomposition, and zirconium boride formed two zirconia silica film, improve the corrosion resistance of the castable, finally with cement mixed material to refractory castable refractory material prepared by the invention has excellent corrosion resistance, erosion resistance and high temperature at the same time after casting properties, good mechanical properties, prolong the service life of refractory castable, has broad application prospects.
【技术实现步骤摘要】
一种耐火浇注料的制备方法
本专利技术公开了一种耐火浇注料的制备方法，属于不定形耐火材料制备
技术介绍
耐火材料是指耐火度不低于1580℃的一类无机非金属材料，因其在高温条件下物理化学性质稳定，而被广泛应用于我国工业生产的各个领域，如钢铁、有色金属、水泥、石化、军工等，是保证行业正常运行和技术革新发展的重要基础支撑材料。耐火材料有很多种分类方式，按照供货形态来分可以分为定型耐火材料和不定型耐火材料。与定形耐火制品相比，不定形耐火材料在生产、劳动生产率、施工效率、材料消耗、改善施工条件、节约能源、环境保护等方面的优越性能，使其在国内外均得到了快速发展。其中，耐火浇注料是一种典型的不定型耐火材料，它是指由合理级配的骨料颗粒、细粉、结合剂及外加剂共同组成的混合料。耐火浇注料通常以干态交货，无固定的外形，使用时加水或其他液体后制成浆状或泥膏状进行浇注施工即可。由于耐火浇注料具有生产工艺简单、可操作性强等优点，因此常被作为热工窑炉和设备的内衬材料使用。然而，现有技术制备的耐火浇注料存在耐高温性能、耐腐蚀性和耐冲刷性差的问题，且耐火浇注料的强度较低，使用寿命短，从而导...
【技术保护点】
一种耐火浇注料，其特征在于，包括以下重量份数的原料：10～15份普通硅酸盐水泥、3～5份高岭土、15～20份铝镁尖晶石、1～3份羧甲基纤维素、40～50份氧化铝、50～60份二氧化硅、10～12份干燥物。
【技术特征摘要】
1.一种耐火浇注料，其特征在于，包括以下重量份数的原料：10～15份普通硅酸盐水泥、3～5份高岭土、15～20份铝镁尖晶石、1～3份羧甲基纤维素、40～50份氧化铝、50～60份二氧化硅、10～12份干燥物。2.所述的干燥物是由硼化锆、甲基三氯硅烷和水混合后冷冻干燥得到的。3.根据权利要求1所述的一...
【专利技术属性】
技术研发人员：王慧文，王维，孙冬，
申请(专利权)人：常州新区金利宝塑料制品有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。