一种激光全息预涂膜及其制备方法技术
Laser holographic precoating film and preparation method thereof
The invention discloses a laser holographic pre coating film, which comprises a base material layer (1), a laser holographic interference fringe, a resin layer (2), a SiO2 coating (3), a ZnS coating (4), a base coating (5), and an adhesive layer (6). The invention also discloses a preparation method. The product of the invention solves the pre coating industry production process, high temperature laser holographic film fade technical problems, ensure the laser holographic effect complete and suitable for high temperature coating, have to provide a BOPP substrate as the representative, laser holographic effect, high temperature resistance, suitable for packaging industry low cost of mass production of new products.
【技术实现步骤摘要】
一种激光全息预涂膜及其制备方法
本专利技术属于现代光学技术与包装
，具体涉及一种激光全息预涂膜及其制备方法。
技术介绍
目前，市场上全息薄膜采用的是模压激光全息图像方式生产。全息成像层使用热塑性树脂，以热模压工序成为干涉条纹，所述的激光全息图像是通过模压光栅条纹层通过光学干涉得以显示。为了避免各种涂胶或覆膜过程中干涉条纹被填平，导致激光全息效果的消失。现在全息薄膜的通用产品设计是将全息成像层朝外和在塑料薄膜面涂胶。因此，存在覆膜受热褪色和受热粘辊的问题。
技术实现思路
本专利技术要解决的技术问题是是一种填补了包装行业空白的新技术，使用特定二种不同光学折射率的透明氧化物及其特定设计工艺的真空镀膜技术工艺，在薄膜为代表的卷材表面，制作激光全息效果和防刮擦和耐高温功能的薄膜及其预涂膜。本专利技术的技术方案为：一种激光全息预涂膜,包括基材层1，激光全息干涉条纹树脂层2，SiO2镀层3，ZnS镀层4，底涂层5，胶粘层6。优选的，所述的基材层为薄膜或纸张或编织布；所述的激光全息模压条纹树脂层(2)厚度范围1-2μm。优选的，所述的薄膜为BOPP、或BOPET、或BOPA、或...
【技术保护点】
一种激光全息预涂膜,其特征在于：包括基材层(1)，激光全息干涉条纹树脂层(2)，SiO2镀层(3)，ZnS镀层(4)，底涂层(5)，胶粘层(6)。
【技术特征摘要】
1.一种激光全息预涂膜,其特征在于：包括基材层(1)，激光全息干涉条纹树脂层(2)，SiO2镀层(3)，ZnS镀层(4)，底涂层(5)，胶粘层(6)。2.根据权利要求1所述的激光全息预涂膜,其特征在于：所述的基材层为薄膜或纸张或编织布；所述的激光全息模压条纹树脂层(2)厚度范围1-2μm。3.根据权利要求2所述的激光全息预涂膜,其特征在于：所述的薄膜为BOPP、或BOPET、或BOPA、或CPP、或复合的透明薄膜，厚度范围是8～40μm。4.根据权利要求1所述的激光全息预涂膜,其特征在于：所述的激光全息模压条纹树脂层为：石蜡或松香或丁醇改性三氯氰胺或PE。5.根据权利要求1所述的激光全息预涂膜，其特征在于：所述的底涂层(5)由聚乙烯亚胺、或乙烯-丙烯酸共聚物、或高分子聚酯水溶液制成。6.根据权利要求5所述的激光全息预涂膜，其特征在于：所述的底涂层的干重≤0.1g/m2，厚度为0.01—0.07μm，固含量为0.7％～5.5％。7.根据权利要求5所述的激...
【专利技术属性】
技术研发人员：许文虓，李建云，
申请(专利权)人：北京康得新功能材料有限公司，
类型：发明
国别省市：北京,11