The invention relates to a high oil absorption resin for treating oily waste water and a preparation method thereof, belonging to the technical field of high oil absorption resin. The invention adopts a suspension polymerization process, using methacrylic acid, isooctyl methacrylate ester, styrene butadiene rubber, eighteen as raw materials, two benzoyl peroxide as initiator, dimethacrylate (1,3) butanediolate as crosslinking agent and porogen was prepared using xylene as high oil absorbing resin. The oil absorption resin on the surface of the water (120# gasoline) adsorption capacity reached 20 30g/g resin, but also has better oil retention rate.
【技术实现步骤摘要】
一种含油废水处理用高吸油树脂及其制备方法
本专利技术涉及一种高吸油树脂及其制备方法，更具体地说，本专利技术涉及一种含油废水处理用高吸油树脂及其制备方法，属于高吸油树脂
技术介绍
随着我国工业化生产的快速发展，包括含油或其他不溶性有机物污水的排放，油船、油罐车的泄漏，大型化工厂、化工原料仓库等化工原料集中贮存地事故的发生，给土壤、河流、海洋及事故发生地周边环境造成了严重的污染，成为日益严重的问题。而传统的吸油材料，如活性炭、黏土、天然纤维织物、聚丙烯纤维等不管是在吸油性能方面，还是在生产能力方面均满足不了油品等有机化合物泄漏事故、废油回收以及油污染环境治理的要求。高吸油性树脂克服了传统吸油材料的缺点，能吸收各种不同的油性物质，特别适用于水面及其它各种固体表面浮油或溢油的吸附回收。同时，还可以用于含油废水的分离净化处理。该类高吸油树脂它具有一定的交联网络结构，较佳的韧性与弹性，还具有良好的刷热性、耐寒性、不易老化、吸油速度快等特点。其浮在水表面，且树脂只吸油不吸水，因此，特别适宜于水面浮油的回收。但是现在的吸油树脂存在保油率低的问题。
技术实现思路
本专利技术旨...
【技术保护点】
一种含油废水处理用高吸油树脂，其特征在于：包括以下按照重量份数计的原料：油相：甲基丙烯酸异辛酯 20‑25份甲基丙烯酸十八酯 15‑20份苯乙烯 10‑15份顺丁橡胶 15‑20份交联剂双甲基丙烯酸（1,3）丁二醇酯 0.3‑0.5份过氧化二苯甲酰 ...
【技术特征摘要】
1.一种含油废水处理用高吸油树脂，其特征在于：包括以下按照重量份数计的原料：油相：甲基丙烯酸异辛酯20-25份甲基丙烯酸十八酯15-20份苯乙烯10-15份顺丁橡胶15-20份交联剂双甲基丙烯酸（1,3）丁二醇酯0.3-0.5份过氧化二苯甲酰1-3份致孔剂二甲苯40份水相：聚乙烯醇5-10份明胶3-5份氯化钠10-15份碳酸钙5-10份去离子水500份。2.根据权利要求1所述的一种含油废水处理用高吸油树脂的制备方法，其特征在于：包括以下工艺步骤：A、称取除了顺丁橡胶以外的油相...