一种锌合金用无铬钝化液制造技术

本发明专利技术公开一种锌合金用无铬钝化液，由以下组份按重量份组成：钼酸钠20‑30份，硫酸钛10‑25份，表面活性剂5‑10份，助剂5‑10份，双氧水30‑40份，稳定剂1‑5份，去离子水30‑50份。本发明专利技术钝化效果较好，钝化膜与镀层的结合力强，经该钝化液处理的锌合金耐腐蚀性能明显提高，且有效避免环境污染问题。

Chromium free passivation liquid for zinc alloy

Non chromium passivation solution of the invention discloses a zinc alloy, consists of the following components by weight portion: 20 sodium molybdate titanium sulfate 10 30 copies, 25 copies, 10 copies of 5 surfactant additives, 5 10 copies, 40 copies of 30 hydrogen peroxide stabilizer, 1 5, deionized water 30 50. The passivation effect of the invention is good, the binding force of the passivation film and the coating is strong, and the corrosion resistance of the zinc alloy treated by the passivation solution is obviously improved, and the environmental pollution problem is effectively avoided.

【技术实现步骤摘要】
一种锌合金用无铬钝化液
本专利技术涉及表面处理
，尤其是指一种锌合金用无铬钝化液。
技术介绍
镀锌及锌合金广泛用于钢铁表面的防护,为提高其抗腐蚀性,增加表面光泽和抗污染能力,镀锌及锌合金后一般要作钝化处理,使其表面生成一层致密稳定性较高的薄膜。现有技术中，通常使用铬酸盐钝化液进行钝化，然而，铬酸盐钝化液含六价铬,毒性大,环境污染严重,镀件在生产和回收过程中易对人体健康产生危害。在无机盐钝化配方和工艺中,高铬酸钝化对环境污染严重,对人体健康产生负面影响,低铬钝化液和超低铬钝化液及其操作工艺减少了环境污染,降低了污水处理费用,但并没有从根本上解决六价铬的污染问题,而且钝化膜的耐蚀性、溶液稳定性和工艺操作等与传统的高铬酸钝化存在差距。随着环保要求的逐步提高，无毒或低毒、高耐蚀性和低成本的钝化工艺将是未来发展的方向。有鉴于此，本专利技术研发出一种克服所述缺陷的锌合金用无铬钝化液，本案由此产生。
技术实现思路
本专利技术的目的在于提供一种锌合金用无铬钝化液，其钝化效果较好，钝化膜与镀层的结合力强，经该钝化液处理的锌合金耐腐蚀性能明显提高，且有效避免环境污染问题。为了达成上述目的，本专利技术的本文档来自技高网...

【技术保护点】
一种锌合金用无铬钝化液，其特征在于：由以下组份按重量份组成：钼酸钠20‑30份，硫酸钛10‑25份，表面活性剂5‑10份，助剂5‑10份，双氧水30‑40份，稳定剂1‑5份，去离子水30‑50份。

【技术特征摘要】
1.一种锌合金用无铬钝化液，其特征在于：由以下组份按重量份组成：钼酸钠20-30份，硫酸钛10-25份，表面活性剂5-10份，助剂5-10份，双氧水30-40份，稳定剂1-5份，去离子水30-50份。2.如权利要求1所述的一种锌合金用无铬钝...

【专利技术属性】
技术研发人员：金碧，孙昇凌，李明仁，
申请(专利权)人：厦门建霖健康家居股份有限公司，
类型：发明
国别省市：福建,35