缓释香精微胶囊的合成技术制造技术

本发明专利技术针对香精微胶囊的合成。本方法以聚乙烯醇做皮材，以玫瑰香精为芯材，用界面聚合法合成香精微胶囊，在一定温度、pH下进行的反应，经过乳化‑聚乙烯醇的溶解‑聚合‑干燥即可，产物无需纯化处理，便可得到最终产物香精微香囊。本发明专利技术涉及的香精微香囊的合成方法简单，所得香精微香囊无需进一步纯化处理，而且合成工艺简单易行，生产成本较低。

Synthesis technology of sustained-release essence microcapsule

The invention aims at the synthesis of microcapsule of essence. The method of using polyvinyl alcohol as skin material, with rose essence as core material, polymerization of microcapsules with the interface, in a certain temperature, pH reaction, after dissolving emulsion polymerization of polyvinyl alcohol drying, the product without purification, we can get the final product flavor micro sachet. The invention relates to a synthesis method of the essence of micro sachet is simple, the essence of micro sachet without further purification, and the synthesis process is simple and the production cost is low.

【技术实现步骤摘要】
缓释香精微胶囊的合成技术
本专利技术涉及缓释香精微胶囊的合成技术。主要适用于生物载体材料。
技术介绍
香精微胶囊在一定压力下会破裂或通过壁材细微孔道缓缓释放香精分子，达到控制释放和长效的目的。玫瑰香精具有抗敏感、保湿、镇定、减压、安眠等作用。普通香精易挥发，使用中存在散发快、热稳定性差、留香时间短等缺点，香精微胶囊的方法控制了香精的释放速度，是使香精缓释长效化的有效途径。聚乙烯醇(Polyvinylalcohol，PVA)是分子结构规整、分子链柔顺的水溶性高分子，具有半结晶结构的白色粉末状树脂。聚乙烯醇具有良好的反应性、生物相容性和无毒性，良好的化学稳定性，与大多的有机溶剂都不发生作用，价廉易得，是一种可应用于发酵工业、医药工业、食品工业、化学工业、环境保护等众多领域且具有发展潜力的生物载体材料。目前，聚乙烯醇作为肥料载体、药物载体、生物载体以及食品添加剂的载体等均已应用。
技术实现思路
本专利技术目的是提供一种低成本，易操作的香精微香囊的合成方法，并且合成的缓释微香囊不仅有缓释效果，还提高了香精的稳定性，延长了散香期。本方法以聚乙烯醇做皮材，用界面聚合法合成香精微胶囊，在一定温度、pH本文档来自技高网...

【技术保护点】
缓释香精微胶囊的合成方法，其原理如下：第一步：

【技术特征摘要】
1.缓释香精微胶囊的合成方法，其原理如下：第一步：第二步：。2.权利1中所述，酸为盐酸；醇为聚乙烯醇；交联剂为戊二醛；聚乙烯醇为皮材；玫瑰香精为芯材。3.权利1中所述，乳化剂为Tween-80和Span-80；交联剂为戊二醛。权利1中所述，第一步中聚乙烯醇的用量为2.0g，第二步的玫瑰香精的用量比为3.0g，聚乙烯醇的用量和玫瑰香精的用量比为2∶3-5，Tween-80和Span-80的用量...