The invention provides an aluminum extrusion preparation process, and relates to the technical field of wood material production, mainly including mixing, granulating, CO extrusion and cooling process; the granulation process, the raw material components and components: Plastic 25 ~ 30%, 0.5 ~ 3% lubricant of wood powder, 30 ~ 50%, coupling agent 1 ~ 5%, 5 ~ 20%, the rest of the talcum powder as processing aids, and above all the components meet 100%. The beneficial effect of energy saving and emission reduction: wood plastic coextrusion profile combining Aluminum Alloy and wood, saving energy consumption and reduce carbon emissions; high strength, ingenious structure of dovetail groove, Aluminum Alloy and the perfect combination of plastic coextrusion ensure the overall rigid plastic, aluminum extrusion profiles.
【技术实现步骤摘要】
一种铝塑共挤制备工艺
：本专利技术涉及塑木材料生产
，尤其涉及一种铝塑共挤制备工艺。
技术介绍
：塑料包装废弃物已严重地污染了环境，影响了工农业生产，危害了人类健康和动植物的生存。世界塑料年产量已超过2亿吨，我国塑料包装材料2007年已超过1000万吨，这些塑料包装材料和容器经一次性使用后，大部分成了固体废弃物。塑料包装废弃物重量轻、体积大、数量多，难以降解，又不能随意焚化，大多被丢弃在铁路边、内河水域和城镇大街小巷，日积月累便成了触目惊心的“白色污染”带。据有关部门调查了解上海日产垃圾1000吨，塑料废弃物约占330吨；北京日产垃圾12000吨，塑料废弃物约占360吨；广州日产垃圾约6000吨，塑料垃圾约占200吨。我国采伐剩余物和造材剩余物约占林木生物量的40％,按照国务院批准的“十一五”期间森林采伐限额2.5亿m3/a计算,我国每年将产生约1.1亿吨的采伐、造材剩余物。另外,加工剩余物按原木的34.4％计算也有高达3210万m3的年产量。目前,虽然林业“三剩物”的利用已经引起人们的重视,但在世界范围内发展水平并不平衡。中国等发展中国家的木材综合利用率仅...
【技术保护点】
一种铝塑共挤制备工艺，其特征在于：铝塑共挤是铝合金与PE塑木紧密复合为一体的复合型材，其制作是将厚度约4mm的表面塑木，复合在铝合金型材表面，达到内金属与外塑木结合一体；因此该型材同时兼容了金属型材有的高精度、高强度和塑木抗腐蚀的优点；主要包括混料、造粒、复合共挤、冷却定型生产过程；造粒过程，所需的原料组分及组分量为：
【技术特征摘要】
1.一种铝塑共挤制备工艺，其特征在于：铝塑共挤是铝合金与PE塑木紧密复合为一体的复合型材，其制作是将厚度约4mm的表面塑木，复合在铝合金型材表面，达到内金属与外塑木结合一体；因此该型材同时兼容了金属型材有的高精度、高强度和塑木抗腐蚀的优点；主要包括混料、造粒、复合共挤、冷却定型生产过程；造粒过程，所需的原料组分及组分量为：以上各组分量之和满足100％；混料过程，将料按配方混合，经过混料机高速搅拌，摩擦生热，至设定的工艺温度110℃～12...
【专利技术属性】
技术研发人员：唐圣卫，唐道远，
申请(专利权)人：安徽森泰木塑集团股份有限公司，
类型：发明
国别省市：安徽,34