The new wood plastic composite material of the invention discloses a method for preparing a greatly improved weathering performance, thermoplastic plastics and wood fiber, high temperature, high temperature lubricant coupling agent are mixed, mixed materials; Carbide Granulation and carbide by extrusion, and regular cooling, traction and cutting, which are wood plastic materials. Carbonation and carbonation, granulating extrusion temperature is 250 to 290 DEG C. The invention of the wood plastic composite material surface and cross-section of black, with a metallic luster, metallic percussion sound; thermal deformation and thermal deformation temperature increase; moisture absorption is decreased, not prone to corrosion and disintegration, good weather resistance; Enhanced UV resistant ability.
【技术实现步骤摘要】
一种耐候性能增强的木塑复合材料的制造方法
本专利技术涉及一种木塑材料及其制备方法，具体涉及一种耐候性能增强的木塑材料及其制备方法。
技术介绍
木塑，即木塑复合材料（Wood-PlasticComposites,WPC），是国内外近年蓬勃兴起的一类新型复合材料，指利用聚乙烯、聚丙烯和聚氯乙烯等，代替通常的树脂胶粘剂，与35～70%以上的木粉、稻壳、秸秆等废植物纤维混合成新的木质材料，再经挤压、模压、注塑成型等塑料加工工艺，生产出的板材或型材。木塑材料主要用于建材、家具、物流包装等行业，应用灵活，可以应用于木材加工的任何领域，取代木材；木塑还是一种环保材料，不含甲醛，可回收循环利用，应用较为广泛，但是木塑也存在以下问题：1、吸水性强，不仅在湿度变化时造成材料的伸缩变形，而且容易让微生物以及微生物分泌的酶类物质随着水分深入到材料内部，发生自内向外的腐蚀与解体，严重影响产品的耐久性。2、耐紫外线能力不足，表面容易发生光氧化反应，导致材料褪色以及表面氧化腐蚀；3、热变形严重，冷热变化产生内部应力，热变形温度偏低，限制了部分应用场景。专利申请CN105733129A公开了一种...
【技术保护点】
一种耐候性能大幅改善的新型木塑复合材料的制备方法，其特征在于经过以下步骤：（1）按下列质量份的组分备料：热塑性塑料100份、木质纤维100～200份、高温润滑剂1～10份、高温偶联剂10～20份；（2）将步骤（1）中的各组分混合均匀，得到混合物料；（3）将步骤（2）的混合物料经碳化造粒和碳化挤压，再经常规冷却、牵引、切割，得到木塑材料，所述碳化造粒和碳化挤压是在常规的多段造粒和多段挤压工序中，将其中温度最高段的温度均提升为250～290℃。
【技术特征摘要】
1.一种耐候性能大幅改善的新型木塑复合材料的制备方法，其特征在于经过以下步骤：（1）按下列质量份的组分备料：热塑性塑料100份、木质纤维100～200份、高温润滑剂1～10份、高温偶联剂10～20份；（2）将步骤（1）中的各组分混合均匀，得到混合物料；（3）将步骤（2）的混合物料经碳化造粒和碳化挤压，再经常规冷却、牵引、切割，得到木塑材料，所述碳化造粒和碳化挤压是在常规的多段造粒和多段挤压工序中，将其中温度最高段的温度均提升为250～290℃。2.根据权利要求1所述的制备方法，其特征在于：所述步骤（1）的热塑性塑料为聚苯乙烯、高密度聚乙烯、低密度聚乙烯、聚乙烯、聚丙烯、聚氯...
【专利技术属性】
技术研发人员：徐开蒙，邓来学，毕天飞，陈婉，朱义鑫，王云，
申请(专利权)人：云南中乾集成房屋有限公司，
类型：发明
国别省市：云南,53