一种PC塑料合金制造技术

本发明专利技术提供一种PC塑料合金，包括如下重量百分比成分：PC80～90％、ASA1～10％、抗氧剂0.5～2％、增韧剂3～10％、润滑剂0.5～2％和流动促进剂1～5％；所述ASA包括如下重量百分比成分：丙烯腈10～20％、苯乙烯50～80％、丙烯酸酯1～10％；所述流动促进剂为含磷有机化合物；本发明专利技术还提供一种所述PC塑料合金的制备方法；本发明专利技术可使PC塑料合金耐候性能显著提升，通过流动促进剂的作用，提高PC塑料合金的加工流动性；加工工艺简单，成本低廉。

A PC plastic alloy

The invention provides a PC plastic alloy, which comprises the following components: the weight percentage of PC80 ~ 90%, ASA1 ~ 10%, 0.5 ~ 2%, antioxidant, toughening agent 3 ~ 10%, 0.5 ~ 2% and the lubricant flow improver 1 ~ 5%; the ASA comprises the following components: 10 weight percent acrylonitrile styrene - 20%, 50 - 80%, 1 ~ 10% of the acrylate; flow improver for phosphorus containing organic compounds; the invention also provides a preparation method of plastic alloy of the PC; the invention can make the weatherability of PC plastic alloy significantly improved, flow through the role of promoter, improve the processability of PC plastic alloy; the processing technology is simple, cost low.

【技术实现步骤摘要】
一种PC塑料合金
本专利技术涉及一种塑料合金，特别涉及一种PC塑料合金。
技术介绍
聚碳酸酯，英文简称PC，是一种性能优良的非结晶热塑性工程塑料，具有突出的抗冲击能力，耐蠕变和尺寸稳定性好，耐热、吸水率低、无毒、介电性能优良，是五大工程塑料中唯一具有良好透明性的产品。目前广泛应用于汽车、电子电气、建筑、办公设备、包装、运动器材、医疗保健等领域。然而聚碳酸酯存在加工流动性不足、耐化学性能较差等缺点。PC/ASA合金材料因综合性能优异应用在很多领域，但是由于ASA的耐候性不佳使其在户外的应用得到很大程度的限制，还有PC材料的加工流动性较差。
技术实现思路
(一)要解决的技术问题本专利技术要解决的技术问题是提供一种PC与ASA相容性能好的、加工流动性和耐候性能好的PC塑料合金。(二)技术方案为解决上述技术问题，本专利技术提供一种PC塑料合金，包括如下重量百分比成分：PC80～90％、ASA1～10％、抗氧剂0.5～2％、增韧剂3～10％、润滑剂0.5～2％和流动促进剂1～5％。进一步的，作为优选的技术方案，所述PC塑料合金包括如下重量百分比成分：PC86％、ASA6％、抗氧剂1％、增韧剂4％、本文档来自技高网...

【技术保护点】
一种PC塑料合金，其特征在于，包括如下重量百分比成分：PC80～90％、ASA1～10％、抗氧剂0.5～2％、增韧剂3～10％、润滑剂0.5～2％和流动促进剂1～5％。