The present invention provides a method of the invention in precision injection molding, injection molding is completed, the first cooling mold, molding a lot of residual stress is not released, and then heated to the melting point of a polymer through the following 12 18 DEG C, cooling, and ultrasonic wave, the residual stress is evenly dispersed and most release, improve the stability of molded products, reduce warpage; after removal in a vacuum environment is heated to the softening point of 8 DEG C 12, due to the vacuum environment without the pressure of the remaining obstacles, internal stress is fully released, the basic can completely eliminate the warpage. The nano silicon dioxide is added to the release agent of the invention, and the release property is improved, and the ageing resistance and the abrasion resistance of the wood plastic surface are improved.
【技术实现步骤摘要】
一种精密注塑方法
本专利技术涉及注塑
，尤其涉及一种精密注塑方法。
技术介绍
注塑成型过程中，聚合物熔体通过流道系统填充到模具型腔内，在型腔内冷却直至固化，然后顶出。在此过程中，聚合物从流体状态到固体状态,其力学行为发生了快速的改变。这些变化导致注塑成型制品内形成不同程度残余应力，并最终导致其翘曲变形。除翘曲变形外，残余应力还会对制品的外观、力学性能及光学性能等产生不利影响。调节注塑的保压压力、温度、速度都可以改善注塑的翘曲变形性，但是对于精密部件不能完全达到理想状态，需要进一步提高注塑技术。
技术实现思路
本专利技术目的就是为了弥补已有技术的缺陷，提供一种精密注塑方法。本专利技术是通过以下技术方案实现的：一种精密注塑方法，步骤为：（1）制作模具，在模具空腔内部涂覆一层脱模剂；（2）将聚合物加热至熔融状态；（3）将所述熔融的聚合物挤入模具型腔，得到模塑制品；（4）冷却模具，使得聚合物完全固化，再加热至聚合物熔点以下12-18℃，施加超声波，再进行冷却至固化，取出模塑制品；（5）将模塑制品放入真空环境中，加热至聚合物软化点以下8-12℃，保温2-3分钟，冷却，即得...
【技术保护点】
一种精密注塑方法，其特征在于，步骤为：（1）制作模具，在模具空腔内部涂覆一层脱模剂；（2）将聚合物加热至熔融状态；（3）将所述熔融的聚合物挤入模具型腔，得到模塑制品；（4）冷却模具，使得聚合物完全固化，再加热至聚合物熔点以下12‑18℃，施加超声波，再进行冷却至固化，取出模塑制品；（5）将模塑制品放入真空环境中，加热至聚合物软化点以下8‑12℃，保温2‑3分钟，冷却，即得。
【技术特征摘要】
1.一种精密注塑方法，其特征在于，步骤为：（1）制作模具，在模具空腔内部涂覆一层脱模剂；（2）将聚合物加热至熔融状态；（3）将所述熔融的聚合物挤入模具型腔，得到模塑制品；（4）冷却模具，使得聚合物完全固化，再加热至聚合物熔点以下12-18℃，施加超声波，再进行冷却至固化，取出模塑制品；（5）将模塑制品放入真空环境中，加热至聚合物软化点以下8-12℃，保温2-3分钟，冷却，即得。2.如权利要求1所述精密注塑方法，其特征在于，所...
【专利技术属性】
技术研发人员：查国东，储振亚，储亮，李云雷，查卫东，
申请(专利权)人：岳西县同兴尼龙橡胶制品有限公司，
类型：发明
国别省市：安徽,34