The invention relates to the technical field of wood processing, in particular to a wood composite flame retardant and a preparation method thereof and an application thereof in the production of flame retardant plywood. For the composite flame retardant plywood, which comprises the following raw materials in parts by weight: 100 polyethylene glycol 60 and sodium bicarbonate 5 15 copies, 0.5 copies, 0.1 polypropylene resin vinyl acetate 30 40 copies and 40 copies of 30 boric acid. Has the synergistic effect between wood composite flame retardant of the invention of the raw materials, has good flame retardant effect, low toxicity, good smoke suppression and environment friendly, and the price is cheap; the use of the wood composite flame retardant prepared flame retardant plywood can significantly improve the performance of flame-retardant plywood, can reach the national standard C grade fire rating requirements; bonding strength and maximum failure load were close to not use the flame retardant processing made of plywood.
【技术实现步骤摘要】
一种用于胶合板的复合阻燃剂及其制备方法
本专利技术涉及木材加工
，具体涉及一种用于胶合板的复合阻燃剂及其制备方法和应用。
技术介绍
人造板是以木材或其他非木材植物为原料，经一定机械加工分离成各种单元材料后，施加或不施加胶粘剂和其他添加剂压合而成的板材或模压制品。人造板主要包括胶合板、刨花板和纤维板三大类，其中胶合板的强度及体积稳定性最好，在实际应用中也最为广泛。胶合板是家具、建筑装修常用材料之一。人造板实际上是一种木质材料，是着火点很低的可燃物，因此常常需要添加阻燃剂进行阻燃处理，阻燃剂质量的好坏将会影响着人造板防火的效果。近年来，随着胶合板产量不断的增加和人们的防火意识在不断提高，市场上出现了多种阻燃剂。虽然阻燃剂在胶合板的应用较为广泛，但现有的阻燃剂仍存在以下问题：阻燃效果不明显、成本较高、抗流失性和耐老化性差、对胶合板的力学性能影响大等问题。因此，开发一种新型具有高性价比的阻燃剂是非常必要的。公开于该
技术介绍
部分的信息仅仅旨在增加对本专利技术的总体背景的理解，而不应当被视为承认或以任何形式暗示该信息构成已为本领域一般技术人员所公知的现有技术。专利技术内...
【技术保护点】
一种用于胶合板的复合阻燃剂，其特征在于，包括以下重量份数的原料：聚乙二醇60‑100份、碳酸氢钠5‑15份、聚丙烯树脂0.1‑0.5份、醋酸乙烯酯30‑40份和硼酸30‑40份。
【技术特征摘要】
1.一种用于胶合板的复合阻燃剂，其特征在于，包括以下重量份数的原料：聚乙二醇60-100份、碳酸氢钠5-15份、聚丙烯树脂0.1-0.5份、醋酸乙烯酯30-40份和硼酸30-40份。2.根据权利要求1所述的用于胶合板的复合阻燃剂，其特征在于，包括以下重量份数的原料：聚乙二醇80份、碳酸氢钠10份、聚丙烯树脂0.3份、醋酸乙烯酯35份和硼酸40份...
【专利技术属性】
技术研发人员：杨金雄，曾连军，杨健，傅文森，
申请(专利权)人：贵港市鑫宏木业有限公司，
类型：发明
国别省市：广西,45